| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.904 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
2.0 |
g/10min |
| 机械性能 |
FlexuralModulus-1%Secant2(InjectionMolded) |
|
ASTMD790 |
1520 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,MD2(32µm) |
|
ASTMD882 |
138 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD2(32µm) |
|
ASTMD882 |
138 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,32µm) |
|
ASTMD882 |
89.6 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,32µm) |
|
ASTMD882 |
41.4 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,32µm) |
|
ASTMD882 |
470 |
% |
| 薄膜 |
TensileElongation-TD(Break,32µm) |
|
ASTMD882 |
800 |
% |
| 薄膜 |
DartDropImpact(32µm,CastFilm) |
|
ASTMD1709A |
45 |
g |
| 光学性能 |
光泽度(45°) |
|
ASTMD2457 |
85 |
|
| 光学性能 |
雾度(31.8µm,铸造薄膜) |
|
ASTMD1003 |
1.7 |
% |