| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.902 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
8.5 |
g/10min |
| 机械性能 |
抗张强度(屈服,注塑) |
|
ASTMD638 |
33.0 |
MPa |
| 机械性能 |
伸长率(屈服,注塑) |
|
ASTMD638 |
9.0 |
% |
| 机械性能 |
弯曲模量(注塑) |
|
ASTMD790 |
1200 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,MD(30µm,BlownFilm) |
|
ASTMD882 |
490 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD(30µm,BlownFilm) |
|
ASTMD882 |
470 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,30µm,BlownFilm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,30µm,BlownFilm) |
|
ASTMD882 |
20.0 |
MPa |
| 薄膜 |
TensileElongation-MD(Yield,30µm,BlownFilm) |
|
ASTMD882 |
14 |
% |
| 薄膜 |
TensileElongation-TD(Yield,30µm,BlownFilm) |
|
ASTMD882 |
13 |
% |
| 薄膜 |
始封温度(30µm,吹塑薄膜) |
|
|
112 |
°C |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,注塑) |
|
ASTMD256 |
45 |
J/m |
| 硬度 |
洛氏硬度(R级,注塑) |
|
ASTMD785 |
100 |
|
| 热性能 |
载荷下热变形温度(0.45MPa,未退火,注塑) |
|
ASTMD648 |
90.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15252 |
139 |
°C |
| 光学性能 |
光泽度(45°,30.0µm,吹塑薄膜) |
|
ASTMD2457 |
97 |
|
| 光学性能 |
雾度(30.0µm,吹塑薄膜) |
|
ASTMD1003 |
2.0 |
% |