| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ISO 1183 |
0.9 |
G/cm3 |
| 熔体流动速率 |
230°C/2.16 kg |
ASTM D1238 |
2 |
g/10min |
| 机械性能 |
拉伸模量 |
|
ISO 527-3 |
| 1% Secant, MD: 50.0 µm, Blown Film |
1% Secant, TD: 50.0 µm, Blown Film |
| 810 |
790 |
|
Mpa |
| 拉伸强度 |
|
ISO 527-3 |
| TD: Break, 50.0 µm, Blown Film |
MD: Break, 50.0 µm, Blown Film |
| 32 |
47 |
|
Mpa |
| 拉伸应变 |
|
ISO 527-3 |
| TD: Break, 50.0 µm, Blown Film |
MD: Break, 50.0 µm, Blown Film |
| 500 |
580 |
|
% |
| 热性能 |
热变形温度 |
0.45Mpa, Unannealed |
ISO 75-2/B |
80 |
℃ |
| 维卡软化温度 |
|
ISO 306/A |
129 |
℃ |
| 光学性能 |
光泽度 |
45°, 50.0 µm, Blown Film |
ASTM D2457 |
80 |
|
| 雾度 |
50.0 µm, Blown Film |
ASTM D1003 |
3 |
% |