ABS | XR-409H
生产厂家：LG化学
规格用途
| 规格级别 |
耐热 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
流动系数 |
200℃，5kg |
ASTM D-1238(G) |
0.3 |
g/10min |
| 流动系数 |
220℃,10kg |
ASTM D-1238(G) |
3.0 |
g/10min |
| 流动系数 |
230℃,3.8kg |
ASTM D-1238(I) |
1.2 |
g/10min |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.05 |
|
| 成型收缩率 |
|
ASTM D-955 |
0.4-0.7 |
% |
| 机械性能 |
IZOD缺口冲击强度 |
1/8",30℃ |
ASTM D-256 |
6(59)(1.1) |
kg.cm/cm(J/m)(ft-lb/in) |
| 伸张率(抗拒点) |
50mm/min |
ASTM D-638 |
>6 |
% |
| IZOD缺口冲击强度 |
1/4",30℃ |
ASTM D-256 |
5(49)(0.9) |
kg.cm/cm(J/m)(ft-lb/in) |
| IZOD缺口冲击强度 |
1/4",23℃ |
ASTM D-256 |
13(127)(2.4) |
kg.cm/cm(J/m)(ft-lb/in) |
| 张力模数 |
1mm/min |
ASTM D-638 |
22700(2220)(322000) |
kg/cm2(MPa)(lb/in2) |
| 洛氏硬度 |
|
ASTM D-955 |
108 |
R Scale |
| 弯曲模数 |
15mm/min |
ASTM D-790 |
24900(2440)(354000) |
kg/cm2(MPa)(lb/in2) |
| IZOD缺口冲击强度 |
1/8",23℃ |
ASTM D-256 |
14(140)(2.6) |
kg.cm/cm(J/m)(ft-lb/in) |
| 弯曲强度 |
15mm/min |
ASTM D-790 |
760(75)(10800) |
kg/cm2(MPa)(lb/in2) |
| 伸张率(破断点) |
50mm/min |
ASTM D-638 |
20 |
% |
| 张力强度 |
50mm/min |
ASTM D-638 |
450(44)(6400) |
kg/cm2(MPa)(lb/in2) |
| 热性能 |
燃烧性 |
1/10" |
UL 94 |
HB |
class |
| 燃烧性 |
1/8" |
UL 94 |
HB |
class |
| 维卡软化点 |
1kg,120℃/h |
ASTM D-1525 |
135(275) |
℃(℉) |
| 热变形温度 |
18.5kg/cm2,1/4"未退火 |
ASTM D-648 |
107(225) |
℃(℉) |
| 维卡软化点 |
5kg,50℃/h |
ASTM D-1525 |
116(241) |
℃(℉) |
| 燃烧性 |
1/8" |
IEC 707 |
FH3-34 |
mm/min |
| 燃烧性 |
1/16" |
IEC 707 |
FH3-34 |
mm/min |
| 热变形温度 |
4.6kg/cm2,1/4"未退火 |
ASTM D-618 |
116(241) |
℃(℉) |
| 热变形温度 |
18.5kg/cm2,1/4"退火 |
ASTM D-648 |
112(234) |
℃(℉) |
| 热变形温度 |
4.6kg/cm2,1/4"退火 |
ASTM D-648 |
119(245) |
℃(℉) |
-
-