| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.23 |
g/cm3 |
| 成型收缩率 |
3.18 mm |
ASTM D955 |
0.3 |
% |
| 吸水率 |
24 hr, 23°C |
ASTM D570 |
0.06 |
% |
机械性能 |
洛氏硬度 |
|
ASTM D785 |
102 |
|
| 压缩强度 |
|
ASTM D695 |
61.4 |
MPa |
| 拉伸模量 |
|
ASTM D638 |
10300 |
MPa |
| 抗张强度 |
|
ASTM D638 |
57.9 |
MPa |
| 拉伸断裂伸长率 |
|
ASTM D638 |
1.5 |
% |
| 弯曲模量 |
|
ASTM D790 |
6550 |
MPa |
| 弯曲强度 |
|
ASTM D790 |
72.4 |
MPa |
| 悬壁梁缺口冲击强度 |
3.18 mm |
ASTM D256 |
74.7 |
J/m |
| 无缺口悬臂梁冲击 |
3.18 mm |
ASTM D256 |
160 |
J/m |
| 热性能 |
热变形温度 |
0.45MPa, 未退火 |
ASTM D648 |
166 |
°C |
| 1.8 MPa, 未退火 |
ASTM D648 |
149 |
°C |
| 阻燃等级 |
|
UL 94 |
HB |
|
| 线形膨胀系数 |
|
ASTM D696 |
0.000032 |
cm/cm/°C |
| 导热系数 |
|
ASTM C177 |
0.36 |
W/m/K |
| 电气性能 |
耐电弧性 |
|
ASTM D495 |
102 |
sec |
| 耗散因数 |
1 MHz |
ASTM D150 |
0.0020 |
|
| 介电常数 |
1 MHz |
ASTM D150 |
3.2 |
|
| 介电强度 |
|
ASTM D149 |
20 |
kV/mm |
| 体积电阻率 |
|
ASTM D257 |
1.0E+15 |
ohm·cm |
| 加工条件 |
螺筒后部温度 |
|
|
218-274 |
°C |
| 螺筒中部温度 |
|
|
218-274 |
°C |
| 螺筒前部温度 |
|
|
218-274 |
°C |
| 干燥温度 |
|
|
82.2 |
°C |
| 干燥时间 |
|
|
2.0 |
hr |
| 模具温度 |
|
|
32.2-65.6 |
°C |
| 注塑温度 |
|
|
68.9-103 |
MPa |
| 建议的最大回制料比例 |
|
|
20 |
% |
|