| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.16 |
g/cm3 |
| 成型收缩率 |
3.18 mm |
ASTM D955 |
0.1-0.3 |
% |
| 吸水率 |
24 hr, 23°C |
ASTM D570 |
0.01 |
% |
| 熔体流动速率 |
230°C/2.16 kg |
ASTM D1238 |
1.5 |
g/10 min |
| 机械性能 |
拉伸模量 |
|
ASTM D638 |
6890 |
MPa |
| 抗张强度 |
|
ASTM D638 |
58.6 |
MPa |
| 拉伸断裂伸长率 |
|
ASTM D638 |
1.5-2.5 |
% |
| 弯曲模量 |
|
ASTM D790 |
5860 |
MPa |
| 弯曲强度 |
|
ASTM D790 |
89.6 |
MPa |
| 悬壁梁缺口冲击强度 |
3.18 mm |
ASTM D256 |
53.4 |
J/m |
| 无缺口悬臂梁冲击 |
3.18 mm |
ASTM D4812 |
214 |
J/m |
| 热性能 |
热变形温度 |
0.45MPa, 未退火 |
ASTM D648 |
160 |
°C |
| 1.8 MPa, 未退火 |
ASTM D648 |
149 |
°C |
| 阻燃等级 |
|
UL 94 |
HB |
|
| 电气性能 |
体积电阻率 |
|
ASTM D257 |
1.0E+14 |
ohm·cm |
| 介电强度 |
|
ASTM D149 |
20 |
kV/mm |
| 介电常数 |
1 MHz |
ASTM D150 |
3 |
|
| 耗散因数 |
1 MHz |
ASTM D150 |
0.0010 |
|
| 耐电弧性 |
1.59 mm |
ASTM D495 |
120 |
sec |
| 加工条件 |
干燥温度 |
|
|
79.4 |
°C |
| 干燥时间 |
|
|
2.0 |
hr |
| 模具温度 |
|
|
32.2-65.6 |
°C |
| 注塑温度 |
|
|
68.9-103 |
MPa |
| 熔体温度 |
|
|
191-232 |
°C |
|