| 规格级别 | 阻燃,增强 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 玻璃纤维增强材料, 30% 填料按重量，阻燃性能，注射成型 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.47 | g/cm3 | |
| 成型收缩率 | ASTM D955 | 0.15-0.3 | % | ||
| 吸水率 | ASTM D570 | 0.03 | % | ||
| 熔体流动速率 | ASTM D1238 | 2-4 | g/10 min | ||
| 机械性能 | 硬度 | ASTM D785 | 105 | ||
| 拉伸模量 | ASTM D638 | 7930 | MPa | ||
| 抗张强度 | ASTM D638 | 68.9 | MPa | ||
| 拉伸断裂伸展率 | ASTM D638 | 2.5-4 | % | ||
| 弯曲模量 | ASTM D790 | 6210 | MPa | ||
| 弯曲强度 | ASTM D790 | 114 | MPa | ||
| 悬壁梁缺口冲击强度 | ASTM D256 | 107 | J/m | ||
| 无缺口悬臂梁冲击 | ASTM D4812 | 534 | J/m | ||
| 热性能 | 热变形温度 | 0.45MPa, 未退火 | ASTM D648 | 157 | °C |
| 1.8 MPa, 未退火 | ASTM D648 | 149 | °C | ||
| 阻燃等级 | 0.800 mm | UL 94 | V-0 | ||
| 3.00 mm | UL 94 | V-0 | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 1.0E+15 | ohm·cm | |
| 介电强度 | ASTM D149 | 18 | kV/mm | ||
| 介电常数 | 1 MHz | ASTM D150 | 3.3 | ||
| 耗散因数 | 1 MHz | ASTM D150 | 0.003 | ||
| 耐电弧性 | 1.59 mm | ASTM D495 | 85 | sec | |