| 规格级别 | 填充,热稳定,增强 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 玻璃纤维增强材料, 25% 填料按重量，云母填料, 15% 填料按重量，热稳定性，注射成型 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.24 | g/cm3 | |
| 成型收缩率 | ASTM D955 | 0.2 | % | ||
| 吸水率 | ASTM D570 | 0.03 | % | ||
| 机械性能 | 硬度 | ASTM D785 | 96 | ||
| 拉伸模量 | ASTM D638 | 8960 | MPa | ||
| 抗张强度 | ASTM D638 | 51.7 | MPa | ||
| 拉伸断裂伸展率 | ASTM D638 | 1 | % | ||
| 弯曲模量 | ASTM D790 | 6210 | MPa | ||
| 弯曲强度 | ASTM D790 | 68.9 | MPa | ||
| 悬壁梁缺口冲击强度 | ASTM D256 | 53.4 | J/m | ||
| 无缺口悬臂梁冲击 | ASTM D4812 | 267 | J/m | ||
| 热性能 | 热变形温度 | 0.45MPa, 未退火 | ASTM D648 | 157 | °C |
| 1.8 MPa, 未退火 | ASTM D648 | 146 | °C | ||
| 线形膨胀系数 - 流动 | ASTM D696 | 0.000036 | cm/cm/°C | ||
| 导热系数 | ASTM C177 | 0.35 | W/m/K | ||
| 阻燃等级 | UL 94 | HB | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 1.0E+15 | ohm·cm | |
| 介电强度 | ASTM D149 | 20 | kV/mm | ||
| 介电常数 | 1 MHz | ASTM D150 | 2.8 | ||
| 耗散因数 | 1 MHz | ASTM D150 | 0.00020 | ||
| 耐电弧性 | 1.59 mm | ASTM D495 | 120 | sec | |