POM | 100F
生产厂家：美国杜邦
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-792 |
1.42 |
|
| 物理性能 |
吸水量 |
Equil.50%R.h.+73℉(+23℃) |
ASTM D-570 |
0.28 |
% |
| 吸水量 |
浸泡均衡点+73℉(+23℃) |
ASTM D-570 |
1.40 |
% |
| 吸水量 |
24hrs浸泡+73℉(+23℃) |
ASTM D-570 |
0.32 |
% |
| 绝缘系数 |
+73℉(+23℃)10²to106Hz |
ASTM D-150 |
3.7 |
|
| 扩散因数 |
+73℉(+23℃)106Hz |
ASTM D-150 |
0.005 |
|
| 机械性能 |
挠曲系数 |
+70℃ |
在25℃下 |
1377 |
MPa |
| 挠曲系数 |
+212℉ |
在25℃下 |
120 |
MPsi |
| 伸张强度 |
+158℉ |
ASTM D-638 |
6.6 |
MPsi |
| 挠曲系数 |
+100℃ |
在25℃下 |
826 |
MPa |
| 伸张强度 |
-68℉ |
ASTM D-638 |
14.7 |
MPsi |
| 负载下之变形 |
2000psi@+122℉(14Mpa@50℃) |
ASTM D-621 |
0.7 |
% |
| 剪力 |
+23℃ |
ASTM D-732 |
65.5 |
MPa |
| 弹性系数 |
+23℃ |
ASTM D-638 |
3100 |
MPa |
| 弹性系数 |
+73℉ |
ASTM D-638 |
450 |
MPsi |
| 压缩应力 |
+73℉@10%Def. |
ASTM D-695 |
17.0 |
MPsi |
| 断裂时之拉力伸张度 |
+73℉(+23℃) |
ASTM D-638 |
75 |
|
| 断裂时之拉力伸张度 |
+212℉(+100℃) |
ASTM D-638 |
>260 |
% |
| lzod冲击强度 |
+73℉ |
ASTM D-256 |
2.3 |
ft.lb/in |
| 挠曲系数 |
+122℃ |
在25℃下 |
516 |
MPa |
| 伸张强度 |
-55℃ |
ASTM D-638 |
101 |
MPa |
| 弯曲降服强度 |
+23℃ |
ASTM D-790 |
96.5 |
MPa |
| 压缩应力 |
+23℃@1%Def. |
ASTM D-695 |
33.1 |
MPa |
| 挠曲系数 |
+73℉ |
在25℃下 |
≥270 |
MPsi |
| 剪力 |
+73℉ |
ASTM D-732 |
9.5 |
MPsi |
| 断裂时之拉力伸张度 |
+250℉(+122℃) |
ASTM D-638 |
>260 |
% |
| 压缩应力 |
+73℉@1%Def. |
ASTM D-695 |
4.8 |
MPsi |
| 挠曲系数 |
-55℃ |
在25℃下 |
3650 |
MPa |
| 摩擦系数 |
+73℉(+23℃)动态 |
ThrustWasherTest3 |
0.20 |
|
| 绝缘强度 |
Short Time,2.3mm |
ASTM D-149 |
19.7 |
MV/m |
| 压缩应力 |
+23℃@10%Def. |
ASTM D-695 |
117 |
MPa |
| 伸张强度 |
+250℉ |
ASTM D-638 |
3.3 |
MPsi |
| 伸张强度 |
+73℉ |
ASTM D-638 |
10.0 |
MPsi |
| 伸张强度 |
+100℃ |
ASTM D-638 |
29.6 |
MPa |
| 洛氏硬度 |
|
ASTM D-785 |
M92,R120 |
|
| 伸张强度 |
+122℃ |
ASTM D-638 |
22.8 |
MPa |
| 挠曲系数 |
+250℉ |
在25℃下 |
75 |
MPsi |
| lzod冲击强度 |
40℃ |
ASTM D-256 |
96.1 |
j/m |
| lzod冲击强度 |
-40℉ |
ASTM D-256 |
1.8 |
ft.lb/in |
| 弯曲降服强度 |
+73℉ |
ASTM D-790 |
14.0 |
MPsi |
| 伸张强度 |
+23℃ |
ASTM D-638、 |
68.9 |
MPa |
| 挠曲系数 |
+158℉ |
在25℃下 |
200 |
MPsi |
| 挠曲系数 |
-68℉ |
在25℃下 |
530 |
MPsi |
| lzod冲击强度 |
+23℃ |
ASTM D-256 |
123 |
j/m |
| 电弧抵抗力 |
120mil(3.1mm) |
ASTM D-495 |
220no tracking |
Sec. |
| 断裂时之拉力伸张度 |
+158℉(+70℃) |
ASTM D-638 |
230 |
% |
| 伸张强度 |
+212℉ |
ASTM D-638 |
4.3 |
MPsi |
| 绝缘强度 |
Short Time,90 mils |
ASTM D-149 |
500 |
V/mil |
| 挠曲系数 |
+23℃ |
25℃下 |
2482 |
MPa |
| 伸张强度 |
+70℃ |
ASTM D-638 |
45.5 |
MPa |
| 热性能 |
线性热膨胀系数 |
+140 to +220℉ |
ASTM D-696 |
7.6 |
10-5in/in.℉ |
| 熔点 |
|
ASTM D-2133 |
347 |
℉ |
| 线性热膨胀系数 |
+85 to +140℉ |
ASTM D-696 |
6.8 |
10-5in/in℉ |
| 可燃烧性 |
|
UL-94 |
94HB |
|
| 线性热膨胀系数 |
-40 to +85℉ |
ASTM D-696 |
5.8 |
10-5in/in℉ |
| 线性热膨胀系数 |
+104 to +150℃ |
ASTM D-696 |
14.9 |
10-5m/m.℃ |
| 热变形温度 |
0.5MPa |
ASTM D-648 |
172 |
℃ |
| 线性热膨胀系数 |
+60 to +104℃ |
ASTM D-696 |
13.7 |
10-5m/m.℃ |
| 线性热膨胀系数 |
+29 to +60℃ |
ASTM D-696 |
12.2 |
10-5m/m.℃ |
| 电阻系数 |
+73℉(+23℃)0.2%H2O |
ASTM D-257 |
1015 |
ohm-cm |
| 热变形温度 |
66psi |
ASTM D-648 |
342 |
℉ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
130 |
℃ |
| 线性热膨胀系数 |
-40 to +29℃ |
ASTM D-696 |
10.4 |
10-5m/m.℃ |
| 线性热膨胀系数 |
+220 to +300℉ |
ASTM D-696 |
8.3 |
10-5in/in.℉ |
| 热变形温度 |
264psi |
ASTM D-648 |
266 |
℉ |
| 熔点 |
|
ASTM D-2133 |
175 |
℃ |
-
-