| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
收缩率 |
流动: 150°C, 30分钟, 0.0360 mm | ASTM D1204 | 2.5 | % |
|
流动: 150°C, 30分钟, 0.0500 mm
|
ASTM D1204 | 2.5 | % | ||
| 横向流动: 150°C, 30分钟, 0.0360 mm | ASTM D1204 | 0.4 | % | ||
| 横向流动: 150°C, 30分钟, 0.0500 mm | ASTM D1204 | 0.4 | % | ||
| 表面张力 | Metallized side (36.0 µm) | ASTM D2578 |
56
|
dyne/cm
|
|
| Metallized side (50.0 µm) | ASTM D2578 | 56 |
dyne/cm
|
||
| 薄膜 |
薄膜厚度 - 经测试 |
36, 50 µm
|
µm | ||
| 可供应的薄膜厚度 |
36, 50 µm
|
µm | |||
| 抗张强度 |
MD: 断裂, 36 µm | ASTM D882 | 177 | MPa | |
| MD: 断裂, 50 µm | ASTM D882 | 167 | MPa | ||
| TD: 断裂, 36 µm | ASTM D882 | 186 | MPa | ||
| TD: 断裂, 50 µm | ASTM D882 | 186 | MPa | ||
| 伸长率 | MD: 断裂, 36 µm | ASTM D882 | 130 | % | |
| MD: 断裂, 50 µm | ASTM D882 | 130 | % | ||
| TD: 断裂, 36 µm | ASTM D882 | 120 | % | ||
| TD: 断裂, 50 µm | ASTM D882 | 120 | % | ||
| 透氧率 | (23°C, 36 µm) | ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
|
| (23°C, 50 µm) | ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
||
| 用量 | 36.0 µm | Internal Method | 19.8 | m²/kg | |
| 50.0 µm | Internal Method | 14.3 | m²/kg | ||
| |
水蒸气透过性 |
37.8°C, 90%RH, 36 µm
|
ASTM F1249 |
0.60
|
g/m²/24 hr
|
| 37.8°C, 90%RH, 50 µm | ASTM F1249 |
0.60
|
g/m²/24 hr
|
||
|
Optical Density
|
36.0 µm
|
Internal Method |
-2.8 到 7.2
|
% | |
|
50.0 µm
|
Internal Method |
-2.8 到 7.2
|
% | ||