| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
收缩率 |
流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 2.5 | % |
|
流动: 150°C, 30分钟, 0.0150 mm
|
ASTM D1204 | 2.5 | % | ||
|
流动: 150°C, 30分钟, 0.0230 mm
|
ASTM D1204 | 2.5 | % | ||
| 横向流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 0.4 | % | ||
| 横向流动: 150°C, 30分钟, 0.0150 mm | ASTM D1204 | 0.4 | % | ||
| 横向流动: 150°C, 30分钟, 0.0230 mm | ASTM D1204 | 0.4 | % | ||
| 表面张力 | Metallized side (12.0 µm) | ASTM D2578 |
56
|
dyne/cm
|
|
| Metallized side (15.0 µm) | ASTM D2578 |
56
|
dyne/cm
|
||
| Metallized side (23.0 µm) | ASTM D2578 | 56 |
dyne/cm
|
||
| 薄膜 |
薄膜厚度 - 经测试 |
12, 15, 23 µm
|
|||
| 可供应的薄膜厚度 |
12, 15, 23 µm
|
||||
| 抗张强度 |
MD: 断裂, 12 µm | ASTM D882 | 206 | MPa | |
| MD: 断裂, 15 µm | ASTM D882 | 186 | MPa | ||
| MD: 断裂, 23 µm | ASTM D882 | 186 | MPa | ||
| TD: 断裂, 12 µm | ASTM D882 | 216 | MPa | ||
| TD: 断裂, 15 µm | ASTM D882 | 206 | MPa | ||
| TD: 断裂, 23 µm | ASTM D882 | 206 | MPa | ||
| 伸长率 | MD: 断裂, 12 µm | ASTM D882 | 100 | % | |
| MD: 断裂, 15 µm | ASTM D882 | 100 | % | ||
| MD: 断裂, 23 µm | ASTM D882 | 100 | % | ||
| TD: 断裂, 12 µm | ASTM D882 | 90 | % | ||
| TD: 断裂, 15 µm | ASTM D882 | 90 | % | ||
| TD: 断裂, 23 µm | ASTM D882 | 90 | % | ||
| 透氧率 | (23°C, 12 µm) | ASTM D3985 |
0.900
|
cm³/m²/24 hr
|
|
| (23°C, 15 µm) | ASTM D3985 | 0.800 |
cm³/m²/24 hr
|
||
| (23°C, 23 µm) | ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
||
| 用量 | 12.0 µm | Internal Method | 59.5 | m²/kg | |
| 15.0 µm | Internal Method | 47.6 | m²/kg | ||
| 23.0 µm | Internal Method | 31.0 | m²/kg | ||
| |
水蒸气透过性 |
37.8°C, 90%RH, 12 µm
|
ASTM F1249 |
0.60
|
g/m²/24 hr
|
|
37.8°C, 90%RH, 15 µm
|
ASTM F1249 | 0.60 |
g/m²/24 hr
|
||
| 37.8°C, 90%RH, 23 µm | ASTM F1249 |
0.60
|
g/m²/24 hr
|
||
|
Optical Density
|
12.0 µm
|
Internal Method |
-2.8 到 7.2
|
% | |
|
15.0 µm
|
Internal Method |
-2.8 到 7.2
|
% | ||
|
23.0 µm
|
Internal Method |
-2.8 到 7.2
|
% | ||