| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
收缩率 |
流动: 150°C, 30分钟, 0.0100 mm
|
ASTM D1204 | 2.5 | % |
|
流动: 150°C, 30分钟, 0.0120 mm
|
ASTM D1204 | 2.5 | % | ||
|
流动: 150°C, 30分钟, 0.0230 mm
|
ASTM D1204 | 2.5 | % | ||
|
流动: 150°C, 30分钟, 0.0360 mm
|
ASTM D1204 | 2.5 | % | ||
|
流动: 150°C, 30分钟, 0.0500 mm
|
ASTM D1204 | 2.5 | % | ||
|
横向流动: 150°C, 30分钟, 0.0100 mm
|
ASTM D1204 | 0.4 | % | ||
|
横向流动: 150°C, 30分钟, 0.0120 mm
|
ASTM D1204 | 0.4 | % | ||
|
横向流动: 150°C, 30分钟, 0.0230 mm
|
ASTM D1204 | 0.4 | % | ||
|
横向流动: 150°C, 30分钟, 0.0360 mm
|
ASTM D1204 | 0.4 | % | ||
|
横向流动: 150°C, 30分钟, 0.0500 mm
|
ASTM D1204 | 0.4 | % | ||
|
表面张力
|
10 µm | ASTM D2578 |
56
|
dyne/cm
|
|
| 12 µm | ASTM D2578 |
56
|
dyne/cm
|
||
| 23 µm | ASTM D2578 |
56
|
dyne/cm
|
||
| 36 µm | ASTM D2578 |
56
|
dyne/cm |
||
| 50 µm | ASTM D2578 |
56
|
dyne/cm
|
||
| 薄膜 |
薄膜厚度 - 经测试 |
10, 12, 23, 36, 50 µm
|
µm | ||
| 可供应的薄膜厚度 |
10, 12, 23, 36, 50 µm
|
µm | |||
| 抗张强度 |
MD: 断裂, 10 µm | ASTM D882 | 206 | MPa | |
| MD: 断裂, 12 µm | ASTM D882 | 206 | MPa | ||
| MD: 断裂, 23 µm | ASTM D882 | 186 | MPa | ||
| MD: 断裂, 36 µm | ASTM D882 | 177 | MPa | ||
| MD: 断裂, 50 µm | ASTM D882 | 167 | MPa | ||
| TD: 断裂, 10µm | ASTM D882 | 216 | MPa | ||
| TD: 断裂, 12µm | ASTM D882 | 216 | MPa | ||
| TD: 断裂, 23µm | ASTM D882 | 206 | MPa | ||
| TD: 断裂, 36µm | ASTM D882 | 186 | MPa | ||
| TD: 断裂, 50µm | ASTM D882 | 186 | MPa | ||
| 伸长率 | MD: 断裂, 10 µm | ASTM D882 | 100 | % | |
| MD: 断裂, 12 µm | ASTM D882 | 100 | % | ||
| MD: 断裂, 23 µm | ASTM D882 | 100 | % | ||
| MD: 断裂, 36 µm | ASTM D882 | 130 | % | ||
| MD: 断裂, 50 µm | ASTM D882 | 130 | % | ||
| TD: 断裂, 10 µm | ASTM D882 | 90 | % | ||
| TD: 断裂, 12 µm | ASTM D882 | 90 | % | ||
| TD: 断裂, 23 µm | ASTM D882 | 90 | % | ||
| TD: 断裂, 36 µm | ASTM D882 | 120 | % | ||
| TD: 断裂, 50 µm | ASTM D882 | 120 | % | ||
| 用量 | 10.0 µm | Internal Method | 71.4 | m²/kg | |
| 12.0 µm | Internal Method | 59.5 | m²/kg | ||
| 23.0 µm | Internal Method | 31.0 | m²/kg | ||
| 36.0 µm | Internal Method | 19.8 | m²/kg | ||
| 50.0 µm | Internal Method | 14.3 | m²/kg | ||
|
透氧率
|
23°C, 10 µm
|
ASTM D3985 |
0.900
|
cm³/m²/24 hr
|
|
|
23°C, 12 µm
|
ASTM D3985 |
0.900
|
cm³/m²/24 hr
|
||
|
23°C, 23 µm
|
ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
||
|
23°C, 36 µm
|
ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
||
|
23°C, 50 µm
|
ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
||
|
水蒸气透过性
|
37.8°C, 90%RH, 10 µm
|
ASTM F1249 |
0.60
|
g/m²/24 hr
|
|
|
37.8°C, 90%RH, 12 µm
|
ASTM F1249 |
0.60
|
g/m²/24 hr
|
||
|
37.8°C, 90%RH, 23 µm
|
ASTM F1249 |
0.60
|
g/m²/24 hr
|
||
| 37.8°C, 90%RH, 36 µm | ASTM F1249 |
0.60
|
g/m²/24 hr
|
||
|
37.8°C, 90%RH, 50 µm
|
ASTM F1249 |
0.60
|
g/m²/24 hr
|
||
| 光学性能 |
Optical Density
|
10.0 µm
|
Internal Method |
-2.8 到 7.2
|
%
|
|
12.0 µm
|
Internal Method |
-2.8 到 7.2
|
%
|
||
|
23.0 µm
|
Internal Method |
-2.8 到 7.2
|
%
|
||
|
36.0 µm
|
Internal Method |
-2.8 到 7.2
|
%
|
||
|
50.0 µm
|
Internal Method |
-2.8 到 7.2
|
%
|
||