| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | 薄膜 管道 片材 | ||
| 备注说明 | 保香 防潮 良好的热封性 食品接触的合规性 粘度，高 阻隔树脂 阻氧 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
密度
|
ASTM D1505 | 1.30 |
g/cm³
|
|
| 机械性能 | 摩擦系数 | 与金属 - 动态 | ASTM D1894 | 0.20 | |
| 薄膜 |
割线模量
|
MD | ASTM D882 | 1720 |
MPa
|
| MD | ASTM D882 | 1760 |
MPa
|
||
|
抗张强度
|
MD: 屈服
|
ASTM D882 | 35.2 |
MPa
|
|
|
TD: 屈服
|
ASTM D882 | 27.6 |
MPa
|
||
|
MD: 断裂
|
ASTM D882 | 40.7 |
MPa
|
||
|
TD: 断裂
|
ASTM D882 | 41.4 |
MPa
|
||
|
伸长率
|
MD: 断裂
|
ASTM D882 | 440 |
%
|
|
|
TD: 断裂
|
ASTM D882 | 450 |
%
|
||
| 氧气传输速率 | 25 µm | ASTM D3985 | 190 |
cm³/m²/24 hr
|
|
|
水气透过率
|
ASTM F1249 | 47 |
g/m²/24 hr
|
||
|
Elmendorf Tear Strength
|
MD
|
ASTM D1922 | 8.1 |
kN/m
|
|
| TD | ASTM D1922 | 8.5 |
kN/m
|
||
|
Graves Tear
|
MD, Unnotched
|
ASTM D1004 | 232.8 |
kN/m
|
|
|
TD, unnotched
|
ASTM D1004 | 219.3 |
kN/m
|
||
|
Spencer Impact
|
ASTM D3420 | 53.4 |
J/cm
|
||
|
热封强度
|
107°C
|
24 |
g/2.5 cm
|
||
|
121°C
|
2500 |
g/2.5 cm
|
|||
|
135°C
|
2300 |
g/2.5 cm
|
|||
|
149°C
|
3000 |
g/2.5 cm
|
|||
| 热性能 | 玻璃转化温度 | DSC | ASTM D3418 | 75.0 |
°C
|
|
熔融温度
|
ASTM D3418 | 255 |
°C
|
||