| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度(23°C) |
|
ISO1183 |
1.26 |
g/cm³ |
| 物理性能 |
吸水率3(平衡,23°C,0.0500mm,50%RH) |
|
ISO62 |
0.21 |
% |
| 物理性能 |
收缩性4 |
MD:200°C,50.0µm |
|
<10 |
% |
| 物理性能 |
收缩性4 |
TD:200°C,50.0µm |
|
<5.0 |
% |
| 薄膜 |
可供应的薄膜厚度 |
|
|
6to300µm |
|
| 薄膜 |
拉伸模量 |
MD:23°C,25µm |
ISO527-3 |
1800 |
MPa |
| 薄膜 |
拉伸模量 |
TD:23°C,25µm |
ISO527-3 |
1800 |
MPa |
| 薄膜 |
拉伸模量 |
MD:23°C,50µm |
ISO527-3 |
1800 |
MPa |
| 薄膜 |
拉伸模量 |
TD:23°C,50µm |
ISO527-3 |
1800 |
MPa |
| 薄膜 |
拉伸模量 |
MD:23°C,100µm |
ISO527-3 |
1600 |
MPa |
| 薄膜 |
拉伸模量 |
TD:23°C,100µm |
ISO527-3 |
1600 |
MPa |
| 薄膜 |
拉伸应力 |
MD:断裂,23°C,25µm |
ISO527-3 |
130 |
MPa |
| 薄膜 |
拉伸应力 |
TD:断裂,23°C,25µm |
ISO527-3 |
130 |
MPa |
| 薄膜 |
拉伸应力 |
MD:断裂,23°C,50µm |
ISO527-3 |
120 |
MPa |
| 薄膜 |
拉伸应力 |
TD:断裂,23°C,50µm |
ISO527-3 |
120 |
MPa |
| 薄膜 |
拉伸应力 |
MD:断裂,23°C,100µm |
ISO527-3 |
120 |
MPa |
| 薄膜 |
拉伸应力 |
TD:断裂,23°C,100µm |
ISO527-3 |
120 |
MPa |
| 薄膜 |
伸长率 |
MD:断裂,23°C,25µm |
ISO527-3 |
>200 |
% |
| 薄膜 |
伸长率 |
TD:断裂,23°C,25µm |
ISO527-3 |
>200 |
% |
| 薄膜 |
伸长率 |
MD:断裂,23°C,50µm |
ISO527-3 |
>200 |
% |
| 薄膜 |
伸长率 |
TD:断裂,23°C,50µm |
ISO527-3 |
>200 |
% |
| 薄膜 |
伸长率 |
MD:断裂,23°C,100µm |
ISO527-3 |
>200 |
% |
| 薄膜 |
伸长率 |
TD:断裂,23°C,100µm |
ISO527-3 |
>200 |
% |
| 薄膜 |
裤型撕裂耐性5 |
MD:50µm |
ISO6383-1 |
6.00 |
N/mm |
| 薄膜 |
裤型撕裂耐性5 |
TD:50µm |
ISO6383-1 |
6.00 |
N/mm |
| 热性能 |
结晶峰温(DSC) |
|
|
143 |
°C |
| 热性能 |
线形热膨胀系数-流动6(0.0500mm) |
|
ASTMD696 |
6.0E-5 |
cm/cm/°C |
| 电气性能 |
体积电阻率7(23°C,0.0500mm) |
|
ASTMD257 |
2.0E+16 |
ohms·cm |
| 电气性能 |
介电强度 |
23°C,0.0250mm |
ASTMD149 |
270 |
kV/mm |
| 电气性能 |
介电强度 |
23°C,0.0500mm8 |
ASTMD149 |
190 |
kV/mm |
| 电气性能 |
介电强度 |
23°C,0.100mm |
ASTMD149 |
120 |
kV/mm |
| 电气性能 |
介电常数(23°C,0.0500mm,10MHz) |
|
ASTMD150 |
3.30 |
|
| 电气性能 |
耗散因数(23°C,0.0500mm,10MHz) |
|
ASTMD150 |
3.0E-3 |
|
| 电气性能 |
DielectricBreakdown |
23°C,25.0µm |
ASTMD149 |
6750 |
V |
| 电气性能 |
DielectricBreakdown |
23°C,50.0µm |
ASTMD149 |
9500 |
V |
| 电气性能 |
DielectricBreakdown |
23°C,125.0µm |
ASTMD149 |
15000 |
V |
| 补充信息 |
PunctureResistance(23°C,50.0µm) |
|
内部方法 |
40.0 |
kJ/m² |