PC/ABS | HR-5006A
生产厂家：LG化学
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
抗低温冲击 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.13 |
|
| 成型收缩率 |
|
ASTM D955 |
0.5-0.8 |
% |
| 机械性能 |
拉伸强度 |
- |
|
ASTM D638 |
560 |
kg/cm2 |
| - |
|
ASTM D638 |
55 |
MPa |
| - |
|
ASTM D638 |
7960 |
psi |
| 断裂伸长率 |
|
ASTM D638 |
＞100 |
% |
| 弯曲强度 |
- |
|
ASTM D790 |
790 |
kg/cm2 |
| - |
|
ASTM D790 |
77 |
MPa |
| - |
|
ASTM D790 |
11200 |
psi |
| 弯曲模量 |
- |
|
ASTM D790 |
22500 |
kg/cm2 |
| - |
|
ASTM D790 |
2205 |
MPa |
| - |
|
ASTM D790 |
320 |
psi |
| Izod缺口冲击强度 |
- |
|
ASTM D256 |
65 |
Kg.cm/cm |
| - |
|
ASTM D256 |
635 |
J/m |
| - |
|
ASTM D256 |
12.0 |
ft.ib/in |
| 洛氏硬度 |
|
ASTM D785 |
110 |
R |
| 热性能 |
熔融指数 |
|
|
4 |
g/10min |
| 热变形温度 |
- |
1.82MPa |
ASTM D648 |
108 |
℃ |
| - |
1.82MPa |
ASTM D648 |
225 |
℉ |
-
-