PC | PC-110
生产厂家：美国陶氏
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
300℃/1.2kg |
ASTM D-1238 |
10 |
g/10min |
| 吸水率 |
24hr,23℃ |
ASTM D-570 |
0.20 |
% |
| 物理性能 |
雾度 |
3.2mmt |
ASTM D-1003 |
＜0.8 |
% |
| 折射率 |
|
ASTM D-542 |
1.585 |
% |
| 比重 |
23/23℃ |
ASTM D-792 |
1.20 |
|
| 成型收缩率 |
|
ASTM D-955 |
0.5-0.7 |
% |
| 全光穿透率 |
3mmt |
ASTM D-570 |
89 |
% |
| 机械性能 |
弯曲模量 |
23℃ |
ASTM D-790 |
24000 |
MPa |
| IZOD冲击强度 |
1/16" |
ASTM D-256 |
87 |
Kg.cm/cm |
| 伸长率 |
屈服点 |
50mm/min |
ASTM D-638 |
6 |
MPa |
| 断裂点 |
- |
ASTM D-638 |
110 |
MPa |
| 洛氏硬度 |
|
ASTM D-785 |
M-77 |
M Scale |
| 弯曲强度 |
23℃ |
ASTM D-790 |
920 |
kg/m2 |
| IZOD冲击强度 |
1/4" |
ASTM D-256 |
14.3 |
Kg.cm/cm |
| 压缩强度 |
|
ASTM D-695 |
780 |
kg/m2 |
| 拉伸强度 |
23℃ |
ASTM D-638 |
630 |
kg/m2 |
| 电气性能 |
介电常数 |
105Hz |
ASTM D-150 |
2.9 |
|
| 耐电弧性 |
|
ASTM D-495 |
110 |
Sec |
| 介电常数 |
60Hz |
ASTM D-150 |
2.95 |
|
| 体积电阻率 |
|
ASTM D-257 |
3 |
×1016Ω.cm |
| 介电损耗 |
60Hz |
ASTM D-150 |
0.0004 |
|
| 绝缘破坏强度 |
1.6mm |
ASTM D-149 |
30 |
KV/mm |
| 介电损耗 |
105Hz |
ASTM D-150 |
0.009 |
|
| 热性能 |
热变形温度 |
未退火,18.6Kg/cm2,120℃/hr |
ASTM D-648 |
125 |
℃ |
| 线膨胀系数 |
40～100℃ |
ASTM D-696 |
6-8 |
×10-5cm/cm/℃ |
| 热变形温度 |
未退火,4.6Kg/cm2,120℃/hr |
ASTM D-648 |
136 |
℃ |
| 热传导率 |
|
ASTM C-177 |
0.2 |
W/m℃ |
| 维卡软化点 |
1Kg,50℃/hr |
ASTM D-1525 |
153 |
℃ |
| 燃烧率 |
1/16" |
UL 94 |
V-2 |
|
-
-
TOP