PC | PC 8600-10
生产厂家：美国陶氏
规格用途
| 规格级别 |
阻燃 其它 注塑 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792,ISO 1183/B |
1.20 |
g/cm3 |
| |
熔体流动速率 |
300℃/1.2kg |
ASTM D1238,ISO 1133 |
10 |
g/10min |
| |
成型收缩率 |
流动 |
ASTM D955 |
0.50-0.70 |
% |
| |
|
流量 |
ISO 294-4 |
0.50-0.70 |
% |
| 硬度 |
洛氏硬度 |
R计秤,3.18mm |
ASTM D785 |
123 |
|
| |
|
R计秤,4.00mm |
ISO 2039-2 |
123 |
|
| 机械性能 |
拉伸模量 |
3.18mm |
ASTM D638 |
2210 |
MPa |
| |
|
4.00mm |
ISO 527-2/50 |
2200 |
MPa |
| |
拉伸强度 |
屈服,3.18mm |
ASTM D638 |
60.0 |
MPa |
| |
|
屈服,4.00mm |
ISO 527-2/50 |
60.0 |
MPa |
| |
|
断裂,3.18mm |
ASTM D638 |
57.9 |
MPa |
| |
|
断裂,4.00mm |
ISO 527-2/50 |
58.0 |
MPa |
| |
伸长率 |
屈服,3.18mm |
ASTM D638 |
6.2 |
% |
| |
|
屈服,4.00mm |
ISO 527-2/50 |
6.0 |
% |
| |
|
断裂,3.18mm |
ASTM D638 |
110 |
% |
| |
|
断裂,4.00mm |
ISO 527-2/50 |
110 |
% |
| |
弯曲模量 |
3.18mm |
ASTM D790 |
2400 |
MPa |
| |
|
4.00mm |
ISO 178 |
2400 |
MPa |
| |
弯曲强度 |
3.18mm |
ASTM D790 |
93.8 |
MPa |
| |
|
4.00mm |
ISO 178 |
94.0 |
MPa |
| |
悬壁梁缺口冲击强度 |
23℃,3.18mm |
ASTM D256 |
747 |
J/m |
| |
|
23℃ |
ISO 180/A |
10.0 |
kJ/m2 |
| |
装有测量仪表的落镖冲击 |
23℃,3.18mm |
ASTM D3763 |
58.8 |
J |
| 热性能 |
热变形温度 |
0.45MPa,未退火 |
ASTM D648,ISO 75-2/B |
139 |
℃ |
| |
|
1.8MPa,未退火 |
ASTM D648 |
127 |
℃ |
| |
|
1.8MPa,未退火 |
ISO 75-2/A |
125 |
℃ |
| |
维卡软化温度 |
|
ASTM D1525 |
149 |
℃ |
| |
|
|
ISO 306/A120 |
150 |
℃ |
| |
|
|
ISO 306/B50 |
144 |
℃ |
| |
球压温度 |
|
IEC 60335-1 |
>125 |
℃ |
| |
线形膨胀系数 |
流动(-22到85℃) |
ASTM D696 |
0.000065 |
cm/cm/℃ |
| 可燃性 |
UL阻燃等级 |
1.59mm |
Internal Method |
V-0 |
|
| |
热灯丝点火温度 |
2.00mm |
IEC 60695-2-13 |
960 |
℃ |
| |
极限氧指数 |
|
ASTM D2863,ISO 4589-2 |
35 |
% |
| UL746 |
RTI Str |
|
UL 746 |
125 |
℃ |
| |
RTI lmp |
|
UL 746 |
125 |
℃ |
| |
RTI Elec |
|
UL 746 |
125 |
℃ |
-
-