| 规格级别 | 阻燃 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D792 |
1.19
|
g/cm³
|
|
| ISO 1183 | 1.20 |
g/cm³
|
|||
| 熔流率 | (300°C/1.2 kg) | ASTM D1238 |
5.0
|
g/10 min
|
|
| 溶化体积流率 | (300°C/1.2 kg) | ISO 1133 |
5.00
|
cm³/10min
|
|
|
收缩率
|
流动 (3.20 mm) | Internal Method |
0.55 到 0.75
|
% | |
|
横向流动 : 3.20 mm
|
Internal Method |
0.60 到 0.80
|
% | ||
|
吸水率
|
饱和, 23°C
|
ISO 62 |
0.14
|
%
|
|
|
平衡, 23°C, 50% RH
|
ISO 62 |
0.11
|
%
|
||
|
室外适用性
|
f1
|
||||
| 机械性能 |
拉伸模量
|
5.0 mm/min | ASTM D638 |
2500
|
MPa |
| ISO 527-2/1 |
2400
|
MPa |
|||
|
抗张强度
|
屈服类型 1, 50 mm/min
|
ASTM D638 |
68
|
MPa
|
|
| 屈服 | ISO 527-2/50 | 67 |
MPa
|
||
|
断裂类型 1, 50 mm/min
|
ASTM D638 |
52
|
MPa
|
||
| 断裂 | ISO 527-2/50 | 52 |
MPa
|
||
|
伸长率
|
屈服类型 1, 50 mm/min
|
ASTM D638 |
6.0
|
%
|
|
| 屈服 | ISO 527-2/50 | 6.0 |
%
|
||
|
断裂类型 1, 50 mm/min
|
ASTM D638 |
51
|
% | ||
| 断裂 | ISO 527-2/50 | 23 |
%
|
||
|
弯曲模量
|
1.3 mm/min (50.0 mm 跨距) | ASTM D790 |
2400
|
MPa
|
|
| 2.0 mm/min | ISO 178 |
2500
|
MPa
|
||
|
弯曲强度
|
1.3 mm/min (屈服, 50.0 mm 跨距) | ASTM D790 |
106
|
MPa
|
|
| 2.0 mm/min | ISO 178 | 103 |
MPa
|
||
| 冲击性能 |
简支梁缺口冲击强度80*10*3 sp=62mm
|
-30°C
|
ISO 179/1eA | 9.0 |
kJ/m²
|
|
23°C
|
ISO 179/1eA |
10
|
kJ/m²
|
||
|
简支梁缺口冲击强度
|
-30°C
|
ISO 179/1eU |
无断裂
|
|
|
|
23°C
|
ISO 179/1eU |
无断裂
|
|||
|
悬壁梁缺口冲击强度
|
-30°C
|
ASTM D256 |
85
|
J/m
|
|
|
23°C
|
ASTM D256 | 100 |
J/m
|
||
|
-30°C 80*10*3
|
ISO 180/1A | 9.0 |
kJ/m²
|
||
|
23°C 80*10*3
|
ISO 180/1A | 10 |
kJ/m²
|
||
| 无缺口伊佐德冲击强度 |
-30°C
|
ISO 180/1U |
无断裂
|
||
| 23°C | ISO 180/1U |
无断裂
|
|||
| 装有测量仪表的落镖冲击 | (23°C, Total Energy) | ASTM D3763 |
66.0
|
J | |
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 3.20 mm
|
ASTM D648 |
131
|
°C
|
|
0.45 MPa, 未退火, 100 mm 跨距120*10*4 mm
|
ISO 75-2/Be |
131
|
°C
|
||
|
1.8 MPa, 未退火, 3.20 mm
|
ASTM D648 |
120
|
°C
|
||
| 1.8 MPa, 未退火, 100 mm 跨距120*10*4 mm | ISO 75-2/Ae | 120 |
°C
|
||
|
维卡软化温度
|
标准 B (120°C/h), 压 力2 (50N) | ASTM D1525 |
136
|
°C
|
|
| ISO 306/B50 | 137 |
°C
|
|||
| ISO 306/B120 | 139 |
°C
|
|||
|
Ball Pressure Test
(125°C)
|
IEC 60695-10-2 |
Pass
|
|||
|
线形膨胀系数
|
流动 (-40 到 40°C)
|
ASTM E831 |
0.000066
|
cm/cm/°C
|
|
|
流动 23 到 80°C)
|
ISO 11359-2 |
0.000072
|
cm/cm/°C
|
||
|
横向 (-40 到 40°C)
|
ASTM E831 |
0.000070
|
cm/cm/°C
|
||
|
横向 23 到 80°C
|
ISO 11359-2 |
0.000076
|
cm/cm/°C
|
||
|
RTI Elec
|
UL 746 |
125
|
°C
|
||
|
RTI Imp
|
UL 746 | 120 |
°C
|
||
|
RTI Str
|
UL 746 |
125
|
°C
|
||
| 电气性能 |
介电常数
|
(1.10 GHz) | ASTM ES7-83 |
2.79
|
|
| 耗散因数 | (1.10 GHz) | ASTM ES7-83 |
0.0058
|
||
| 可燃性 |
UL 阻燃等级
|
0.400 mm
|
UL 94 |
V-2
|
|
|
1.00 mm
|
UL 94 |
V-0
|
|||
|
3.00 mm
|
UL 94 | 5VA | |||
|
灼热丝易燃指数
(1.20mm)
|
IEC 60695-2-12 |
960
|
°C
|
||
|
热灯丝点火温度
(1.20 mm)
|
IEC 60695-2-13 | 875 |
°C
|
||
| 注射 |
干燥温度
|
121 |
°C
|
||
|
干燥时间
|
3到4 |
hr
|
|||
| 干燥时间,最大 | 48 |
hr
|
|||
|
建议的最大水分含量
|
0.020 | % | |||
|
建议注入量
|
40 到 60
|
%
|
|||
|
螺筒后部温度
|
266 到 288
|
°C
|
|||
|
螺筒中部温度
|
277 到 299
|
°C
|
|||
|
螺筒前部温度
|
288 到 310
|
°C
|
|||
|
射嘴温度
|
282 到 304
|
°C
|
|||
|
加工（熔体）温度
|
288 到 310
|
°C
|
|||
|
模具温度
|
71.1 到 93.3
|
°C
|
|||
|
背压
|
0.345 到 0.689
|
MPa
|
|||
|
螺杆转速
|
40 到 70
|
rpm | |||
|
排气孔深度
|
0.025 到 0.076
|
mm | |||