| 规格级别 | 阻燃 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D792 |
1.20
|
g/cm³
|
|
| ASTM D792 | 1.19 |
g/cm³
|
|||
|
特定体积
|
ASTM D792 |
0.830
|
cm³/g
|
||
| 熔流率 | (300°C/1.2 kg) | ASTM D1238 | 7 |
g/10 min
|
|
| 溶化体积流率 | 300°C/1.2 kg | ISO 1133 | 7.0 |
cm³/10min
|
|
| 收缩率 - 流动 | (3.20 mm) | Internal Method |
0.50到 0.70
|
%
|
|
|
吸水率
|
24 hr
|
ASTM D570 |
0.15
|
%
|
|
|
平衡, 23°C
|
ASTM D570 |
0.35
|
%
|
||
|
平衡, 100°C
|
ASTM D570 |
0.58
|
%
|
||
|
室外适用性
|
UL 746C |
f2
|
|||
| 硬度 |
洛氏硬度
|
M 计秤
|
ASTM D785 |
70
|
|
|
R 计秤
|
ASTM D785 | 118 | |||
| 机械性能 |
抗张强度
|
屈服,Type I, 5 mm/min | ASTM D638 |
62.1
|
MPa
|
| 屈服 | ISO 527-2/50 |
63.0
|
MPa
|
||
| 断裂,Type I, 5 mm/min | ASTM D638 | 65.5 |
MPa
|
||
| 断裂 | ISO 527-2/50 |
63.0
|
MPa
|
||
|
伸长率
|
屈服,Type I, 5 mm/min | ASTM D638 | 7.0 |
%
|
|
| 屈服 | ISO 527-2/50 | 6.0 | % | ||
| 断裂,Type I, 5 mm/min | ASTM D638 | 110 |
%
|
||
|
弯曲模量
|
50.0 mm 跨距,1.3 mm/min | ASTM D790 | 2340 |
MPa
|
|
| 50.0 mm 2.0 mm/min | ISO 178 | 2300 |
MPa
|
||
|
弯曲强度
|
屈服, 50.0 mm 跨距,1.3 mm/min | ASTM D790 | 93.0 |
MPa
|
|
| 50.0 mm 2.0 mm/min | ISO 178 |
94.0
|
MPa
|
||
| 抗泰伯磨耗 | (1000 Cycles, 1000 g, CS-17 转轮) | ASTM D1044 |
10.0
|
mg | |
| 冲击性能 |
悬壁梁缺口冲击强度
|
23°C
|
ASTM D256 | 750 |
J/m
|
|
无缺口悬臂梁冲击
|
23°C
|
ASTM D4812 | 3200 |
J/m
|
|
| 落锤冲击 | (23°C) | ASTM D3029 |
169
|
J | |
| 拉伸冲击强度 | Type S | ASTM D1822 |
546
|
kJ/m²
|
|
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 |
°C
|
|
1.8 MPa, 未退火, 6.40 mm
|
ASTM D648 | 132 |
°C
|
||
|
维卡软化温度
|
标准 B (120°C/h), 压 力2 (50N) | ASTM D1525 |
154
|
°C
|
|
| ISO 306/B120 | 145 |
°C
|
|||
| Ball Pressure Test | (125°C) |
Pass
|
IEC 60695-10-2
|
||
|
线形膨胀系数
|
流动: -40 到 95°C
|
ASTM E831 |
0.000068
|
cm/cm/°C
|
|
|
比热
|
|
ASTM C351 |
1260
|
J/kg/°C
|
|
|
导热系数
|
ASTM C177 |
0.29
|
W/m/K
|
||
|
RTI Elec
|
UL 746 |
130
|
°C
|
||
|
RTI Imp
|
UL 746 |
125
|
°C
|
||
|
RTI Str
|
UL 746 |
125
|
°C
|
||
| 电气性能 |
体积电阻率
|
ASTM D257 |
> 1.0E+17
|
ohm·cm
|
|
|
介电强度
|
(3.20 mm, in Air) | ASTM D149 |
15
|
kV/mm
|
|
|
介电常数
|
50 Hz
|
ASTM D150 | 3.17 | ||
|
60 Hz
|
ASTM D150 | 3.17 | |||
|
1 MHz
|
ASTM D150 | 2.96 | |||
|
耗散因数
|
50 Hz
|
ASTM D150 |
0.00090
|
||
|
60 Hz
|
ASTM D150 |
0.00090
|
|||
|
1 MHz
|
ASTM D150 | 0.010 | |||
|
相比耐漏电起痕指数(CTI)
|
UL 746A | 3 |
PLC code
|
||
|
高电弧燃烧指数(HAI)
|
UL 746A | 1 |
PLC code
|
||
|
热丝引燃 (HWI)
|
UL 746A | 3 |
PLC code
|
||
| 可燃性 | UL 阻燃等级 | 0.750 到 3.00 mm |
V-2
|
UL 94 | |
|
灼热丝易燃指数
|
0.750 mm
|
IEC 60695-2-12 | 750 |
°C
|
|
| 1.50mm | IEC 60695-2-12 | 850 |
°C
|
||
|
热灯丝点火温度
|
0.750 mm by VDE
|
IEC 60695-2-13 | 875 |
°C
|
|
|
1.50 mm
|
IEC 60695-2-13 | 850 |
°C
|
||
| 光学性能 | 透射率 | 2540 µm | ASTM D1003 | 88.0 | % |
| 雾度 | 2540 µm | ASTM D1003 | 1.0 | % | |
| 注射 |
干燥温度
|
120 |
°C
|
||
|
干燥时间
|
3到4 |
hr
|
|||
|
干燥时间，最大
|
48 |
hr
|
|||
|
建议的最大水分含量
|
0.02 | % | |||
|
建议注入量
|
40到60 | % | |||
|
螺筒后部温度
|
290 到 310
|
°C
|
|||
|
螺筒中部温度
|
300 到 320
|
°C
|
|||
|
螺筒前部温度
|
310 到 330
|
°C
|
|||
|
射嘴温度
|
305 到 325
|
°C
|
|||
|
加工（熔体）温度
|
310 到 330
|
°C
|
|||
|
模具温度
|
80到115
|
°C
|
|||
|
背压
|
0.3到0.7
|
MPa | |||
|
螺杆转速
|
40 到 70
|
rpm | |||
|
排气孔深度
|
0.025 到 0.076
|
mm | |||