| 规格级别 | 耐磨 其它 其它 | 外观颜色 | 半透明 |
| 该料用途 | 工程配件 | ||
| 备注说明 | 耐磨损性良好 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
|
ASTM D792 |
1.26
|
g/cm³
|
|
收缩率
|
流动 | ASTM D955 |
0.50到 0.70
|
% | |
| 横向流动 | ASTM D955 |
0.50到 0.70
|
% | ||
|
横向流量
|
ISO 294-4 |
0.50到 0.70
|
%
|
||
|
流量
|
ISO 294-4 |
0.50到 0.70
|
%
|
||
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.17 | % | |
| 机械性能 |
洛氏硬度
(M 计秤)
|
ASTM D785 |
67
|
||
|
拉伸模量
|
--
|
ASTM D638 | 2300 |
MPa
|
|
| -- | ISO 527-2/1 | 2400 |
MPa
|
||
|
抗张强度
|
屈服
|
ASTM D638 | 55.0 |
MPa
|
|
|
屈服
|
ISO 527-2/50 | 50.0 |
MPa
|
||
|
断裂
|
ASTM D638 | 51.0 |
MPa
|
||
|
断裂
|
ISO 527-2/50 | 50.0 |
MPa
|
||
|
伸长率
|
屈服
|
ISO 527-2/50 | 6.0 |
%
|
|
| 断裂 | ASTM D638 | 110 | % | ||
|
弯曲模量
|
--
|
ASTM D790 | 2110 |
MPa
|
|
|
-- 3
|
ISO 178 | 2200 | MPa | ||
|
弯曲强度
|
-- 3
|
ISO 178 |
80.0
|
MPa
|
|
|
屈服
|
ASTM D790 | 78.0 | MPa | ||
|
压缩强度
|
ASTM D695 | 73.0 | MPa | ||
|
简支梁缺口冲击强度
|
ISO 179 | 25 |
kJ/m²
|
||
|
简支梁缺口冲击强度
|
ISO 179 | 无断裂 |
|
||
|
悬壁梁缺口冲击强度
|
3.20 mm
|
ASTM D256 | 290 |
J/m
|
|
|
6.40 mm
|
ASTM D256 |
120
|
J/m
|
||
| 热性能 |
热变形温度
|
0.45 MPa, 未退火
|
ASTM D648 | 145 | ℃ |
|
0.45 MPa, 未退火
|
ISO 75-2/B | 139 | ℃ | ||
|
1.8 MPa, 未退火
|
ASTM D648 | 136 | ℃ | ||
|
1.8 MPa, 未退火
|
ISO 75-2/A | 130 | ℃ | ||
|
维卡软化温度
|
ISO 306/B50 |
141
|
℃ | ||
|
线形膨胀系数
|
流动 | ASTM D696 |
7.0E-5
|
cm/cm/℃
|
|
| 横向 | ASTM D696 |
7.0E-5
|
cm/cm/℃
|
||
| RTI Elec | 1.47 mm | UL 746 |
115
|
℃ | |
| RTI Imp | 1.47 mm | UL 746 |
105
|
℃ | |
| RTI Str | 1.47 mm | UL 746 |
105
|
℃ | |
| 电气性能 |
表面电阻率
|
IEC 60093 |
1.0E+15
|
ohm
|
|
|
体积电阻率
|
--
|
ASTM D257 |
1.0E+18
|
ohm·cm
|
|
| -- | IEC 60093 |
1.0E+15
|
ohm·cm
|
||
|
介电强度
|
1.60 mm 4
|
ASTM D149 |
30
|
kV/mm
|
|
| -- | IEC 60243-1 | 32 |
kV/mm
|
||
|
介电常数
|
60 Hz
|
ASTM D150 |
2.85
|
||
|
1 MHz
|
ASTM D150 |
2.80
|
|||
|
100 Hz
|
IEC 60250 | 3.00 | |||
|
1 MHz
|
IEC 60250 |
3.00
|
|||
|
耗散因数
|
60 Hz
|
ASTM D150 |
8.0E-4
|
||
|
1 MHz
|
ASTM D150 |
8.0E-3
|
|||
|
100 Hz
|
IEC 60250 |
1.0E-3
|
|||
|
1 MHz
|
IEC 60250 |
9.0E-3
|
|||
|
耐电弧性
|
ASTM D495 |
100
|
sec
|
||
|
相比耐漏电起痕指数(CTI)
|
UL 746 | 340 |
V
|
||
|
漏电起痕指数
|
IEC 60112 | 300 |
V
|
||
| 可燃性 |
UL 阻燃等级
|
1.50mm
|
UL 94 |
V-2
|
|