| 规格级别 | 高流动 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 共聚物、流动性高、延展性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792, ISO 1183 | 1.20 |
g/cm
3
|
|
|
熔流率
|
300℃/1.2 kg | ASTM D1238 | 40 |
g/10 min
|
|
| 溶化体积流率（MVR） | 300℃/1.2 kg | ISO 1133 | 38.0 |
cm
3/10min
|
|
| 收缩率 |
流动: 3.20 mm
|
Internal Method |
0.50 到 0.70
|
%
|
|
|
吸水率
|
饱和, 23
℃
|
ISO 62 | 0.30 |
%
|
|
|
平衡, 23
℃
, 50% RH
|
0.15 |
%
|
|||
| 机械性能 |
洛氏硬度
|
R 计秤 | ASTM D785 | 120 | |
|
拉伸模量
|
ASTM D638 | 2270 | MPa | ||
| ISO 527-2/1 | 2180 | MPa | |||
| 抗张强度 |
屈服
|
ASTM D638 | 60.0 |
MPa
|
|
|
屈服
|
ISO 527-2/50 | 63.0 |
MPa
|
||
| 断裂 | ASTM D638 | 56.0 | MPa | ||
| 断裂 | ISO 527-2/50 | 56.0 | MPa | ||
| 伸长率 |
屈服
|
ASTM D638 | 5.5 |
%
|
|
|
屈服
|
ISO 527-2/50 | 6.0 |
%
|
||
| 断裂 | ASTM D638 | 130 | % | ||
| 断裂 | ISO 527-2/50 | 97 | % | ||
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2240 |
MPa
|
|
| ISO 178 | 2180 | MPa | |||
| 弯曲强度 | ISO 178 | 91.0 | MPa | ||
| 屈服, 50.0 mm 跨距 | ASTM D790 | 100 | MPa | ||
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eA | 13 |
kJ/m
2
|
|
| 23℃ | 64 | kJ/m2 | |||
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eU |
无断裂
|
||
| 23℃ |
无断裂
|
||||
|
悬壁梁缺口冲击强度
|
-30℃ | ASTM D256 | 110 |
J/m
|
|
| 0℃ | ASTM D256 | 700 | J/m | ||
| 23℃ | ASTM D256 | 730 | J/m | ||
| -30℃ | ISO 180/1A | 11 | kJ/m2 | ||
| 23℃ | ISO 180/1A | 58 | kJ/m2 | ||
|
无缺口伊佐德冲击强度
|
-30℃ | ISO 180/1U |
无断裂
|
||
| 23℃ |
无断裂
|
||||
| 装有测量仪表的落镖冲击 | 23℃, Total Energy | ASTM D3029 | 56.0 |
J
|
|
| ISO 6603-2 | 95.0 | J | |||
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 3.20 mm
|
ASTM D648 | 121 | ℃ |
|
1.8 MPa, 未退火, 3.20 mm
|
ASTM D648 | 110 | ℃ | ||
| 1.8 MPa, 未退火, 64.0 mm 跨距 | ISO 75-2/Af | 115 | ℃ | ||
|
维卡软化温度
|
ASTM D1525 | 135 | ℃ | ||
| ISO 306/B50 | 129 | ℃ | |||
| ISO 306/B120 | 130 | ℃ | |||
| Ball Pressure Test | 125℃ | IEC 60695-10-2 |
Pass
|
||
| 线形膨胀系数 |
流动: -40 到 40
℃
|
ASTM E831, ISO 11359-2 |
0.000030
|
cm/cm/
℃
|
|
|
横向:
-40 到 40
℃
|
0.000070
|
cm/cm/℃ | |||
|
RTI Elec
|
UL 746 | 105 | ℃ | ||
|
RTI Imp
|
UL 746 | 105 | ℃ | ||
|
RTI Str
|
UL 746 | 105 | ℃ | ||
| 可燃性 |
UL 阻燃等级
|
0.300 mm
|
UL 94 |
HB
|
|
| 光学性能 |
折射率
|
ASTM D542 | 1.582 | ||
|
透射率
|
2540 µm | ASTM D1003 | 88.0 |
%
|
|
| 雾度 | 2540 µm | ASTM D1003 |
< 1.0
|
%
|
|