| 规格级别 | 耐热 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 尺寸稳定性良好、耐热性中等、食品接触的合规性、中等透明度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 1.19 |
g/cm
3
|
|
| 1.19 | g/cm3 | ||||
|
特定体积
|
ASTM D792 | 0.830 | cm3/g | ||
|
熔流率
|
300℃/1.2 kg | ASTM D1238 | 25 |
g/10 min
|
|
| 溶化体积流率（MVR） | 300℃/1.2 kg | ISO 1133 |
23.0
|
cm3/10 min | |
| 收缩率 | 流动 (3.20 mm) | Internal Method |
0.50 到 0.70
|
%
|
|
|
吸水率
|
24 hr
|
ASTM D570 | 0.15 |
%
|
|
|
平衡, 23
℃
|
0.35 |
%
|
|||
|
平衡, 100
℃
|
0.58 |
%
|
|||
| 机械性能 |
洛氏硬度
|
M 计秤
|
ASTM D785 | 70 | |
|
R 计秤
|
118 | ||||
|
拉伸模量
|
ASTM D638 | 2370 | MPa | ||
| ISO 527-2/1 | 2350 | MPa | |||
| 抗张强度 |
屈服
|
ASTM D638 | 62.0 |
MPa
|
|
| 屈服 | ISO 527-2/50 | 63.0 | MPa | ||
|
断裂
|
ASTM D638 | 65.0 |
MPa
|
||
| 断裂 | ISO 527-2/50 | 65.0 | MPa | ||
| 伸长率 |
屈服
|
ASTM D638 | 6.0 |
%
|
|
| 屈服 | ISO 527-2/50 | 6.0 | % | ||
|
断裂
|
ASTM D63 | 120 |
%
|
||
| 断裂 | ISO 527-2/50 | 70 | % | ||
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2300 |
MPa
|
|
| ISO 178 | 2300 | MPa | |||
| 弯曲强度 | ISO 178 | 90.0 | MPa | ||
| 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 | MPa | ||
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 |
mg
|
|
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eA | 12 |
kJ/m
2
|
|
| 23℃ | 12 | kJ/m2 | |||
|
悬壁梁缺口冲击强度
|
Natural, Tints
|
ASTM D256 | 640 |
J/m
|
|
| 23℃ | ASTM D256 | 640 | J/m | ||
| -30℃ | ISO 180/1A | 10 | kJ/m2 | ||
| 23℃ | ISO 180/1A | 12 | kJ/m2 | ||
|
无缺口悬臂梁冲击
|
23℃ | ASTM D4812 | 3200 |
J/m
|
|
| 有测量仪表的落镖冲击 | 23℃, Energy at Peak Load | ASTM D3763 | 54.0 | J | |
| 落锤冲击 | 23℃ | ASTM D3029 | 169 |
J
|
|
| 拉伸冲击强度 | ASTM D1822 | 378 | kJ/m2 | ||
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 6.40 mm
|
ASTM D648 | 137 | ℃ |
| 0.45 MPa, 未退火, 100 mm 跨距 | ISO 75-2/Be | 133 | ℃ | ||
|
1.8 MPa, 未退火, 3.20 mm
|
ASTM D648 | 129 | ℃ | ||
|
1.8 MPa, 未退火, 6.40 mm
|
ASTM D648 | 126 | ℃ | ||
| 1.8 MPa, 未退火, 100 mm 跨距 | ISO 75-2/Ae | 121 | ℃ | ||
|
维卡软化温度
|
ISO 306/B50 | 139 | ℃ | ||
| ISO 306/B120 | 140 | ℃ | |||
| Ball Pressure Test | 125℃ | IEC 60695-10-2 |
Pass
|
||
|
线形膨胀系数 - 流动
|
-40 到 95℃ | ASTM E831 |
0.000068
|
cm/cm/
℃
|
|
|
23 到 80
℃
|
ISO 11359-2 |
0.000070
|
cm/cm/
℃
|
||
|
比热
|
ASTM C351 | 1250 |
J/kg/
℃
|
||
|
导热系数
|
ASTM C177 | 0.19 |
W/m/K
|
||
| ISO 8302 | 0.20 | W/m/K | |||
|
RTI Elec
|
UL 746 | 130 | ℃ | ||
|
RTI Imp
|
UL 746 | 130 | ℃ | ||
|
RTI Str
|
UL 746 | 130 | ℃ | ||
| 电气性能 |
表面电阻率
|
IEC 60093 | > 1.0E+15 | ohm | |
|
体积电阻率
|
ASTM D257 |
> 1.0E+17
|
ohm·cm
|
||
| IEC 60093 | > 1.0E+15 | ohm·cm | |||
| 介电强度 | 3.20 mm, in Air | ASTM D149 | 15 |
kV/mm
|
|
|
3.20 mm, 在油中
|
IEC 60243-1 | 17 | kV/mm | ||
|
介电常数
|
50 Hz
|
ASTM D150 | 3.17 | ||
|
60 Hz
|
ASTM D150 | 3.17 | |||
|
1 MHz
|
ASTM D150 | 2.96 | |||
| 50 Hz | IEC 60250 | 2.70 | |||
| 60 Hz | IEC 60250 | 2.70 | |||
| 1 MHz | IEC 60250 | 2.70 | |||
|
耗散因数
|
50 Hz
|
ASTM D150 | 0.00090 | ||
|
60 Hz
|
ASTM D150 | 0.00090 | |||
|
1 MHz
|
ASTM D150, IEC 60250 | 0.010 | |||
|
50 Hz
|
IEC 60250 | 0.0010 | |||
|
60 Hz
|
IEC 60250 | 0.0010 | |||
|
相比耐漏电起痕指数(CTI)
|
UL 746 |
PLC 2
|
|||
|
高电弧燃烧指数(HAI)
|
UL 746 |
PLC 1
|
|||
|
高电压电弧起痕速率 (HVTR)
|
UL 746 |
PLC 2
|
|||
|
热丝引燃 (HWI)
|
UL 746 |
PLC 2
|
|||
| 可燃性 |
UL 阻燃等级
|
1.09 mm)
|
UL 94 |
V-2
|
|
|
极限氧指数
|
ISO 4589-2 | 25 |
%
|
||
| 光学性 |
折射率
|
ASTM D542 | 1.586 | ||
| 透射率 | 2540 µm | ASTM D1003 | 88.0 |
%
|
|
| 雾度 | 2540 µm | ASTM D1003 | 1.0 |
%
|
|