| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.33 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(300°C/1.2kg) |
|
ASTMD1238 |
15 |
g/10min |
| 物理性能 |
收缩率-流动 |
|
ASTMD955 |
0.20to0.40 |
% |
| 机械性能 |
拉伸模量(3.20mm,注塑) |
|
ASTMD638 |
4000 |
MPa |
| 机械性能 |
TensileStrength(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
100 |
MPa |
| 机械性能 |
TensileElongation(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
4.0 |
% |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.20mm,注塑) |
|
ASTMD256 |
110 |
J/m |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
145 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
140 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,退火) |
|
ASTMD648 |
143 |
°C |
| 电气性能 |
表面电阻率 |
|
ASTMD257 |
3.0E+14 |
ohms |
| 电气性能 |
VolumeResistivity(1.80mm) |
|
ASTMD257 |
1.0E+16 |
ohms·cm |
| 电气性能 |
介电强度(1.60mm) |
|
ASTMD149 |
27 |
kV/mm |
| 电气性能 |
DielectricConstant(1.60mm,1MHz) |
|
ASTMD150 |
3.10 |
|
| 电气性能 |
漏电起痕指数(3.00mm) |
|
IEC60112 |
175 |
V |
| 可燃性 |
FlameRating2(1.5mm) |
|
UL94 |
V-0 |
|