| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.19 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/3.8kg) |
|
ASTMD1238 |
18 |
g/10min |
| 物理性能 |
收缩率-流动 |
|
ASTMD955 |
0.40to0.70 |
% |
| 机械性能 |
TensileStrength(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
65.0 |
MPa |
| 机械性能 |
TensileElongation(Break,3.20mm,InjectionMolded) |
|
ASTMD638 |
70 |
% |
| 机械性能 |
FlexuralModulus(3.20mm,InjectionMolded) |
|
ASTMD790 |
2650 |
MPa |
| 机械性能 |
FlexuralStrength(3.20mm,InjectionMolded) |
|
ASTMD790 |
96.5 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.20mm,注塑) |
|
ASTMD256 |
150 |
J/m |
| 硬度 |
洛氏硬度(R级,3.20mm,注塑) |
|
ASTMD785 |
123 |
|
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
100 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
90.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15252 |
116 |
°C |
| 热性能 |
线形热膨胀系数-流动 |
|
ASTMD696 |
6.6E-5 |
cm/cm/°C |
| 可燃性 |
UL阻燃等级3 |
0.50mm |
UL94 |
V-2 |
|
| 可燃性 |
UL阻燃等级3 |
0.8mm |
UL94 |
V-1 |
|
| 可燃性 |
UL阻燃等级3 |
1.0mm |
UL94 |
V-0 |
|
| 可燃性 |
UL阻燃等级3 |
2.0mm |
UL94 |
5VB |
|