| 规格级别 | 透明,阻燃 其它 注塑 | 外观颜色 | 清晰/透明 |
| 该料用途 | |||
| 备注说明 | 共聚物、耐刮擦性、阻燃性能 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 1.20 |
g/cm
3
|
|
| ISO 1183,ASTM D792 | 1.17 | g/cm3 | |||
|
特定体积
|
ASTM D792 | 0.850 | cm3/g | ||
|
熔流率
|
300℃/1.2 kg | ASTM D1238 | 15 |
g/10 min
|
|
| 溶化体积流率（MVR） | 300℃/1.2 kg | ISO 1133 | 13.5 |
cm
3/10min
|
|
| 收缩率 |
流动: 3.20 mm
|
Internal Method |
0.50 到 0.80
|
%
|
|
|
吸水率
|
24 hr, 50% RH
|
ASTM D570 | 0.040 |
%
|
|
|
24 hr,
|
ASTM D570 | 0.080 |
%
|
||
|
饱和, 23
℃
|
ISO 62 | 0.27 | % | ||
|
平衡, 23
℃
|
ASTM D570 | 0.28 | % | ||
|
平衡, 50% RH
|
ASTM D570 | 0.13 | % | ||
|
平衡, 23
℃
, 50% RH
|
ISO 62 | 0.13 | % | ||
| 机械性能 |
洛氏硬度
|
L 计秤
|
ASTM D785 | 108 | |
|
M 计秤
|
93 | ||||
| 球压硬度 | H 358/30 | ISO 2039-1 | 128 |
MPa
|
|
|
Erichson Scratch Depth - 6N
|
Internal Method | 14.0 |
µm
|
||
| Pencil Hardness | ASTM D3363 |
H
|
|||
|
拉伸模量
|
ASTM D638 | 2900 | MPa | ||
| ISO 527-2/1 | 2450 | MPa | |||
| 抗张强度 |
屈服
|
ASTM D638 | 80.0 |
MPa
|
|
|
屈服
|
ISO 527-2/50 | 80.0 |
MPa
|
||
| 断裂 | ASTM D638 | 65.0 | MPa | ||
| 断裂 | ISO 527-2/50 | 60.0 | MPa | ||
| 伸长率 |
屈服
|
ASTM D638 | 7.0 |
%
|
|
|
屈服
|
ISO 527-2/50 | 7.0 |
%
|
||
| 断裂 | ASTM D638 | 70 | % | ||
| 断裂 | ISO 527-2/50 | 40 | % | ||
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2600 |
MPa
|
|
| ISO 178 | 2450 | MPa | |||
| 弯曲强度 | ISO 178 | 108 | MPa | ||
| 屈服, 50.0 mm 跨距 | ASTM D790 | 120 | MPa | ||
|
抗泰伯磨耗
|
1000 Cycles, 1000 g, CS-17 转轮
|
ASTM D1044 | 10.0 |
mg
|
|
|
1000 Cycles, 1000 g, CS-17 转轮
|
Internal Method | 10.0 |
mg
|
||
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eA | 3.0 |
kJ/m
2
|
|
| 23℃ | 3.0 | kJ/m2 | |||
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eU | 47 | kJ/m2 | |
| 23℃ |
无断裂
|
||||
|
悬壁梁缺口冲击强度
|
-30℃ | ASTM D256 | 30 |
J/m
|
|
| 23℃ | ASTM D256 | 30 | J/m | ||
| -30℃ | ISO 180/1A | 4.0 | kJ/m2 | ||
| 23℃ | ISO 180/1A | 5.0 | kJ/m2 | ||
|
无缺口悬臂梁冲击
|
23℃ | ASTM D4812, ISO 180/1U | 无断裂 | ||
| -30℃ | ISO 180/1U | 45 | kJ/m2 | ||
| 装有测量仪表的落镖冲击 | 23℃, Total Energy | ASTM D3763 | 30.0 |
J
|
|
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 3.20 mm
|
ASTM D648 | 133 | ℃ |
|
0.45 MPa, 未退火, 64.0 mm 跨距
|
ISO 75-2/Bf | 131 | ℃ | ||
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 119 | ℃ | ||
| 1.8 MPa, 未退火, 64.0 mm 跨距 | ISO 75-2/Af | 118 | ℃ | ||
|
维卡软化温度
|
ASTM D1525 | 139 | ℃ | ||
| ISO 306/B50 | 138 | ℃ | |||
| ISO 306/B120 | 140 | ℃ | |||
| Ball Pressure Test | 125℃ | IEC 60695-10-2 |
Pass
|
||
| 140℃ | Pass | ||||
| 线形膨胀系数 |
流动: -40 到 40
℃
|
ASTM E831 |
0.000030
|
cm/cm/
℃
|
|
|
流动: 23 到 80
℃
|
ISO 11359-2 |
0.000030
|
cm/cm/℃ | ||
|
流动:
-40 到 40
℃
|
ASTM E831 |
0.000070
|
cm/cm/℃ | ||
|
流动: 23 到 80
℃
|
ISO 11359-2 | 0.000070 | cm/cm/℃ | ||
|
比热
|
ASTM C351 | 1400 |
J/kg/
℃
|
||
|
导热系数
|
ASTM C177, ISO 8302 | 0.20 |
W/m/K
|
||
| 可燃性 |
UL 阻燃等级
|
1.50 mm, Testing by SABIC
|
UL 94 |
V-2
|
|
|
3.00 mm, Testing by SABIC
|
V-0
|
||||
| 光学性能 |
折射率
|
ASTM D542, ISO 489 | 1.584 | ||
| 透射率 | 2540 µm | ASTM D1003 | 88.0 |
%
|
|
| 雾度 | 2540 µm | ASTM D1003 |
< 0.80
|
%
|
|