| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.20 |
g/cm³ |
| 物理性能 |
密度 |
|
ISO1183/B |
1.20 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(300°C/1.2kg) |
|
ASTMD1238 |
3.0 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率）(300°C/1.2kg) |
|
ISO1133 |
3.0 |
g/10min |
| 机械性能 |
拉伸模量(4.00mm,注塑) |
|
ASTMD638 |
2200 |
MPa |
| 机械性能 |
拉伸模量(4.00mm,注塑) |
|
ISO527-2 |
2200 |
MPa |
| 机械性能 |
TensileStrength(Yield,4.00mm,InjectionMolded) |
|
ASTMD638 |
61.0 |
MPa |
| 机械性能 |
TensileStress(Yield,4.00mm,InjectionMolded) |
|
ISO527-2 |
61.0 |
MPa |
| 机械性能 |
TensileStrength(Break,4.00mm,InjectionMolded) |
|
ASTMD638 |
68.0 |
MPa |
| 机械性能 |
拉伸应力(断裂,4.00mm,注塑) |
|
ISO527-2 |
68.0 |
MPa |
| 机械性能 |
TensileElongation(Yield,4.00mm,InjectionMolded) |
|
ASTMD638 |
6.0 |
% |
| 机械性能 |
TensileStrain(Yield,4.00mm,InjectionMolded) |
|
ISO527-2 |
6.0 |
% |
| 机械性能 |
TensileElongation(Break,4.00mm,InjectionMolded) |
|
ASTMD638 |
100 |
% |
| 机械性能 |
拉伸应变(断裂,4.00mm,注塑) |
|
ISO527-2 |
100 |
% |
| 机械性能 |
FlexuralModulus(4.00mm,InjectionMolded) |
|
ASTMD790 |
2300 |
MPa |
| 机械性能 |
FlexuralModulus(4.00mm,InjectionMolded) |
|
ISO178 |
2300 |
MPa |
| 机械性能 |
FlexuralStrength(4.00mm,InjectionMolded) |
|
ASTMD790 |
90.3 |
MPa |
| 机械性能 |
FlexuralStress(4.00mm,InjectionMolded) |
|
ISO178 |
90.0 |
MPa |
| 冲击性能 |
简支梁缺口冲击强度(23°C,注塑) |
|
ISO179/1eA |
72 |
kJ/m² |
| 冲击性能 |
NotchedIzodImpact(23°C,4.00mm,InjectionMolded) |
|
ASTMD256 |
850 |
J/m |
| 热性能 |
载荷下热变形温度(0.45MPa,退火) |
|
ASTMD648 |
145 |
°C |
| 热性能 |
热变形温度(0.45MPa,退火) |
|
ISO75-2/B |
145 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
132 |
°C |
| 热性能 |
热变形温度(1.8MPa,未退火) |
|
ISO75-2/A |
132 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15252 |
158 |
°C |
| 热性能 |
维卡软化温度 |
|
ISO306/B50 |
158 |
°C |
| 可燃性 |
UL阻燃等级4(1.5mm) |
|
UL94 |
HB |
|