PC | 303V-10
生产厂家：美国Styron
规格用途
| 规格级别 |
透明,耐热,脱模 其它 其它 |
外观颜色 |
|
| 该料用途 |
电子元器件，照明，存储介质外壳 |
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792,ISO 1183/A |
1.20 |
g/cm3 |
| |
熔流率 |
|
ASTM D1238 |
10 |
g/10min |
| |
熔流率 |
300℃/1.2kg |
ISO 1133 |
10 |
g/10min |
| |
流动收缩率 |
|
ASTM D955 |
0.50-0.70 |
% |
| |
流量收缩率 |
|
ISO 294-4 |
0.50-0.70 |
% |
| |
吸水率 |
24hr |
ASTM D570 |
0.15 |
% |
| |
|
23℃,24hr |
ISO 62 |
0.15 |
% |
| |
|
平衡 |
ASTM D570 |
0.32 |
% |
| |
|
平衡，23℃，50%RH |
ISO 62 |
0.32 |
% |
| 机械性能 |
拉伸模量 |
|
ASTM D638 |
2410 |
MPa |
| |
|
|
ISO 527-2/50 |
2300 |
MPa |
| |
屈服抗张强度 |
|
ASTM D638,ISO 527-2/50 |
60.0 |
MPa |
| |
断裂抗张强度 |
|
ASTM D638,ISO 527-2/50 |
71.0 |
MPa |
| |
屈服伸长率 |
|
ASTM D638,ISO 527-2/50 |
6.0 |
% |
| |
断裂伸长率 |
|
ASTM D638,ISO 527-2/50 |
150 |
% |
| |
弯曲模量 |
|
ASTM D790 |
2410 |
MPa |
| |
弯曲模量 |
|
ISO 178 |
2400 |
MPa |
| |
弯曲强度 |
|
ISO 178 |
97.0 |
MPa |
| |
屈服弯曲强度 |
|
ASTM D790 |
96.5 |
MPa |
| |
抗泰伯磨耗 |
|
ASTM D1044 |
45.0 |
mg |
| |
简支梁缺口冲击强度 |
23℃ |
ISO 179/1eA |
35 |
kJ/cm2 |
| |
悬壁梁缺口冲击强度 |
|
ASTM D256 |
910 |
J/m
|
| |
|
23℃ |
ISO 180/4A |
35 |
kJ/cm2 |
| |
无缺口悬壁梁冲击 |
23℃ |
ASTM D256,ISO 180 |
无断裂 |
|
| |
装有测量仪表的落镖冲击 |
|
ASTM D3763 |
87.0 |
J |
| 热性能 |
热变形温度 |
0.45MPa,退火 |
ASTM D648,ISO 75-2/B |
141 |
℃ |
| |
|
1.8MPa,未退火 |
ASTM D648 |
125 |
℃ |
| |
|
1.8MPa,未退火 |
ISO 75-2/A |
122 |
℃ |
| |
|
1.8MPa,退火 |
ASTM D648 |
138 |
℃ |
| |
|
1.8MPa,退火 |
ISO 75-2/A |
143 |
℃ |
| |
维卡软化温度 |
|
ASTM D1525,ISO 306/B50 |
146 |
℃ |
| |
球压温度 |
|
IEC 60335-1 |
125 |
℃ |
| |
流动线形膨胀系数 |
|
ASTM D696 |
0.000068 |
cm/cm/℃ |
| |
UL 阻燃等级 |
1.60 mm |
UL 94 |
V-2 |
|
| |
|
3.20 mm |
UL 94 |
V-2 |
|
| |
极限氧指数 |
|
ISO 4589-2 |
26 |
% |
| 电气性能 |
体积电阻率 |
|
ASTM D257 |
2.0E+17 |
ohm.cm |
| |
介电强度 |
|
ASTM D149,IEC 60243-1 |
17 |
kV/mm |
| |
介电常数 |
60Hz |
ASTM D150 |
3.00 |
|
| |
|
1 MHz |
ASTM D150 |
3.00 |
|
| |
耗散因数 |
|
ASTM D150 |
0.0010 |
|
| |
漏电起痕指数 |
2.00mm,解决方案A |
IEC 60112 |
250 |
V |
| 光学性能 |
折射率 |
|
ASTM D542 |
1.586 |
|
| |
折射率 |
|
ISO 489 |
1.586 |
|
| |
透射率 |
|
ASTM D1003 |
89.0 |
% |
| |
雾度 |
|
ASTM D1003 |
1.0 |
% |
-
-