| 规格级别 | 抗紫外线,脱模,阻燃 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 脱模、紫外线稳定剂、阻燃性能 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能
|
比重
|
ASTM D792 | 1.19 |
g/cm
3
|
|
|
特定体积
|
ASTM D792 | 0.830 | cm3/g | ||
|
熔流率
|
300℃/1.2 kg | ASTM D1238 | 18 |
g/10 min
|
|
| 收缩率 | 流动 (3.20 mm) | Internal Method |
0.50 到 0.70
|
%
|
|
|
吸水率
|
24 hr
|
ASTM D570 | 0.15 |
%
|
|
|
平衡, 23
℃
|
0.35 |
%
|
|||
|
平衡, 100
℃
|
0.58 |
%
|
|||
|
室外适用性
|
UL 746C |
f1
|
|||
| 机械性能 |
洛氏硬度
|
M 计秤
|
ASTM D785 | 70 | |
|
R 计秤
|
118 | ||||
| 抗张强度 |
屈服
|
ASTM D638 | 62.1 |
MPa
|
|
|
断裂
|
65.5 |
MPa
|
|||
| 伸长率 |
屈服
|
ASTM D638 | 7.0 |
%
|
|
|
断裂
|
110 |
%
|
|||
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2340 |
MPa
|
|
| 弯曲强度 | 屈服, 50.0 mm 跨距 | 93.1 | MPa | ||
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 |
mg
|
|
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eA | 12 |
kJ/m
2
|
|
| 23℃ | 65 | kJ/m2 | |||
| 简支梁缺口冲击强度 |
-30
℃
|
ISO 179/1eU |
无断裂
|
||
| 23℃ |
无断裂
|
||||
|
悬壁梁缺口冲击强度
|
23℃ | ASTM D256 | 690 |
J/m
|
|
| -30℃ | ISO 180/1A | 11 | kJ/m2 | ||
| 23℃ | ISO 180/1A | 65 | kJ/m2 | ||
|
无缺口悬臂梁冲击
|
23℃ | ASTM D4812 | 3200 |
J/m
|
|
| -30℃ | ISO 180/1U | 无断裂 | |||
| 23℃ | ISO 180/1U | 无断裂 | |||
| 落锤冲击 | 23℃ | ASTM D3029 | 169 |
J
|
|
| 拉伸冲击强度 | ASTM D1822 | 546 | kJ/m2 | ||
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 6.40 mm
|
ASTM D648 | 138 | ℃ |
|
1.8 MPa, 未退火, 6.40 mm
|
132 | ℃ | |||
|
维卡软化温度
|
ASTM D1525 | 154 | ℃ | ||
| 线形膨胀系数 | 流动 (-40 到 95℃) | ASTM E831 |
0.000068
|
cm/cm/
℃
|
|
|
比热
|
ASTM C351 |
1260
|
J/kg/
℃
|
||
|
导热系数
|
ASTM C177 | 0.25 |
W/m/K
|
||
|
RTI Elec
|
UL 746 | 100 | ℃ | ||
|
RTI Imp
|
UL 746 | 100 | ℃ | ||
|
RTI Str
|
UL 746 | 100 | ℃ | ||
| 电气性能 |
体积电阻率
|
ASTM D257 |
> 1.0E+17
|
ohm·cm
|
|
| 介电强度 | 3.20 mm, in Air | ASTM D149 | 15 |
kV/mm
|
|
|
介电常数
|
50 Hz
|
ASTM D150 | 3.17 | ||
|
60 Hz
|
3.17 | ||||
|
1 MHz
|
2.96 | ||||
|
耗散因数
|
50 Hz
|
ASTM D150 | 0.00090 | ||
|
60 Hz
|
0.00090 | ||||
|
1 MHz
|
0.010 | ||||
|
相比耐漏电起痕指数(CTI)
|
UL 746 |
PLC 2
|
|||
|
高电弧燃烧指数(HAI)
|
UL 746 |
PLC 1
|
|||
|
高电压电弧起痕速率 (HVTR)
|
UL 746 |
PLC 2
|
|||
|
热丝引燃 (HWI)
|
UL 746 |
PLC 4
|
|||
| 可燃性 |
UL 阻燃等级
|
0.750 mm
|
UL 94 |
V-2
|
|
|
5.99 mm
|
V-0
|
||||
| 光学性 |
折射率
|
ASTM D542 | 1.586 | ||
| 透射率 | 2540 µm | ASTM D1003 | 88.0 |
%
|
|
| 雾度 | 2540 µm | ASTM D1003 | 1.0 |
%
|
|