| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
300°C/1.2 kg |
ASTM D1238 |
10 |
g/10 min |
| 吸水率 |
24 hr, 23°C |
ASTM D570 |
0.15 |
% |
| 吸水率 |
Equilibrium, 23°C, 50% RH |
ASTM D570 |
0.32 |
% |
| 物理性能 |
比重 |
|
ASTM D792 |
1.2 |
g/cm3 |
| 模件收缩率 |
|
ASTM D955 |
0.5-0.7 |
% |
| 机械性能 |
硬度 |
R-Scale |
ASTM D785 |
118 |
|
| 硬度 |
M-Scale |
ASTM D785 |
73 |
|
| 拉伸模量 |
|
ASTM D638 |
2410 |
Mpa |
| 屈服抗张强度 |
23°C |
ASTM D638 |
6 |
Mpa |
| 屈服抗张伸展率 |
|
ASTM D638 |
6 |
% |
| 弯曲模量 |
|
ASTM D790 |
2410 |
Mpa |
| 弯曲强度 |
|
ASTM D790 |
96.5 |
Mpa |
| 耐磨性 |
1000 g; CS-10 F wheel; 500 cycles |
ASTM D1044 |
45 |
% |
| 缺口冲击强度 |
23°C, 3.18 mm |
ASTM D256 |
907 |
J/m |
| 仪器化落锤冲击强度 |
23°C, 3.18 mm, Total Energy |
ASTM D3763 |
87 |
J |
| 断裂抗张伸展率 |
|
ASTM D638 |
150 |
% |
| 断裂抗张强度 |
|
ASTM D638 |
71 |
Mpa |
| 电气性能 |
体积电阻率 |
23°C |
ASTM D257 |
2.0E+17o |
ohm.cm |
| 绝缘强度 |
|
ASTM D149 |
17 |
KV/mm |
| 介电常数 |
60 Hz |
ASTM D150 |
3 |
|
| 介电耗损 |
60 Hz |
ASTM D150 |
0.001 |
|
| 相对漏电起痕指数 |
2.00 mm |
ICE 60112 |
250 |
v |
| 热性能 |
未退火热变形温度 |
0.45 MPa, 4.00 mm |
ASTM D648 |
144 |
℃ |
| 退火热变形温度 |
1.8 MPa, 4.00 mm |
ASTM D648 |
128 |
℃ |
| 热变形温度 |
1.8 MPa,退火4.00 mm |
ASTM D648 |
141 |
℃ |
| 维卡软化点 |
|
ASTM D1525 |
149 |
℃ |
| 压痕温度 |
|
IEC 60589-1 |
＞125 |
℃ |
| CLTE-流 |
-40 to 82°C |
ASTM D696 |
0.000068 |
cm/cm/℃ |
| 其它性能 |
火焰等级 |
1.60 mm |
UL 94 |
HB |
|
| 火焰等级 |
3.20 mm |
UL 94 |
HB |
|
| 电线着火温度 |
2.00 mm, 5.0 sec |
CIEC 60695-2-13 |
850 |
℃ |
| 氧指数 |
|
ASTM D2863 |
26 |
% |
| 平均燃烧值 |
|
ASTM D635 |
3 |
cm |
| 光学性能 |
折射率 |
|
ASTM D542 |
1.586 |
|
| 透光率 |
|
ASTM D1003 |
89 |
% |
| 雾度 |
|
ASTM D1003 |
0.7-1.5 |
% |