| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.62 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(250°C/2.16kg) |
|
ASTMD1238 |
4.0to12 |
g/10min |
| 物理性能 |
收缩率-流动(3.18mm) |
|
ASTMD955 |
0.30to0.50 |
% |
| 机械性能 |
抗张强度(屈服,3.17mm) |
|
ASTMD638 |
114 |
MPa |
| 机械性能 |
TensileStrength(Break,3.18mm) |
|
ASTMD638 |
114 |
MPa |
| 机械性能 |
弯曲模量(3.17mm) |
|
ASTMD790 |
7240 |
MPa |
| 机械性能 |
FlexuralStrength(Break,3.18mm) |
|
ASTMD790 |
176 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C,3.18mm) |
|
ASTMD256 |
53 |
J/m |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火,3.18mm) |
|
ASTMD648 |
210 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火,3.18mm) |
|
ASTMD648 |
199 |
°C |
| 热性能 |
RTIElec(6.0to6.6mm) |
|
UL746 |
75.0 |
°C |
| 热性能 |
RTIImp(6.0to6.6mm) |
|
UL746 |
75.0 |
°C |
| 热性能 |
RTIStr(6.0to6.6mm) |
|
UL746 |
75.0 |
°C |
| 电气性能 |
Hot-wireIgnition(HWI)(6.0to6.6mm) |
|
UL746 |
PLC0 |
|
| 可燃性 |
FlameRating(6.0to6.6mm,All) |
|
UL94 |
V-0 |
|