| 规格级别 | 增强,高光泽 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 尺寸稳定性良好、光泽高、良好的成型性能、良好的电气性能、耐化学性良好、耐热性高 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.46 | g/cm3 | |
| 收缩率 | 流动 | ASTM D-955 | 0.25-1.3 | % | |
| 机械性能 | 洛氏硬度 | ASTM D-785 | 120 | R Scale | |
| 抗张强度 | ASTM D-638 | 108 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 2.1 | % | ||
| 弯曲模量 | ASTM D-790 | 6860 | MPa | ||
| 弯曲强度 | ASTM D-790 | 177 | MPa | ||
| 悬臂梁缺口冲击强度 | ASTM D-256 | 68.6 | J/m | ||
| 悬臂梁无缺口冲击强度 | 392 | ||||
| 热性能 | 热变形温度 | 1.8MPa，未退火 | ASTM D-648 | 204 | ℃ |
| UL阻燃等级 | 0.760mm | UL 94 | HB | ||
| 1.57mm | |||||
| 3.18mm | |||||
| RTI Str | 0.760mm | UL 746 | 75.0 | ℃ | |
| 1.57mm | |||||
| 3.18mm | |||||
| RTI Imp | 0.760mm | ||||
| 1.57mm | |||||
| 3.18mm | |||||
| RTI Elec | 0.760mm | ||||
| 1.57mm | |||||
| 3.18mm | |||||