| 规格级别 | 玻纤增强 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 20%玻纤增强，高强度，耐热稳定，耐化学性好，良好的尺寸稳定性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.43 | ||
| 熔融指数 | 250℃/2.16KG | ASTM D1238 | 15 | g/10min | |
| 成型收缩率 | ASTM D955 | 0.002-0.01 | mm/mm | ||
| 吸湿率 | 23℃，50%RH，24hr | ASTM D570 | 0.004 | ||
| 23℃，50%RH，饱和 | ASTM D570 | 0.0018 | |||
| 机械性能 | 拉伸强度 | ASTM D570 | 90 | MPa | |
| 断裂伸长率 | ASTM D570 | 2.6 | % | ||
| 弯曲强度 | ASTM D790 | 164 | MPa | ||
| 弯曲模量 | ASTM D790 | 7000 | MPa | ||
| 缺口冲击强度 | ASTM D256 | 8.5 | KJ/m2 | ||
| 洛氏硬度 | R | ASTM D785 | 120 | ||
| 热性能 | 热变形温度 | 0.45MPa | ASTM D648 | 215 | ℃ |
| 1.82MPa | ASTM D648 | 200 | ℃ | ||
| 线性热膨胀系数 | ASTM D696 | 2.5X10-5 | mm/mm/℃ | ||
| 电气性能 | 介电强度 | ASTM D149 | 20 | KV/mm | |
| 介电常数 | 60Hz | ASTM D150 | 3.2 | ||
| 1MHz | ASTM D150 | 3.5 | |||
| 体积电阻率 | ASTM D257 | 1.0X1016 | Ω.m | ||
| 可燃性 | 水平燃烧 | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | |||