PA66 | T-661
生产厂家：日本东洋
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.14 |
g/cm3 |
| |
流动收缩率 |
1.00mm |
ASTM D955 |
0.60-1.2 |
% |
| |
|
3.00mm |
ASTM D955 |
1.5-2.2 |
% |
| |
吸水率 |
24 hr |
ASTM D570 |
1.2 |
% |
| |
|
平衡，65%RH |
ASTM D570 |
2.5 |
% |
| |
洛氏硬度 |
R 计秤 |
ASTM D785 |
120 |
|
| 机械性能 |
屈服抗张强度 |
-40℃ |
ASTM D638 |
110 |
MPa |
| |
|
23℃ |
ASTM D638 |
50.0 |
MPa |
| |
|
80℃ |
ASTM D638 |
28.0 |
MPa |
| |
断裂伸长率 |
23℃ |
ASTM D638 |
200 |
% |
| |
弯曲模量 |
-40℃ |
ASTM D790 |
4000 |
MPa |
| |
|
23℃ |
ASTM D790 |
1400 |
MPa |
| |
|
80℃ |
ASTM D790 |
600 |
MPa |
| |
屈服弯曲强度 |
-40℃ |
ASTM D790 |
120 |
MPa |
| |
|
23℃ |
ASTM D790 |
66.0 |
MPa |
| |
|
80℃ |
ASTM D790 |
40.0 |
MPa |
| |
压缩强度 |
23℃ |
ASTM D695 |
90.0 |
MPa |
| |
抗泰伯磨耗 |
1000Cycles,CS-17转轮 |
ASTM D1044 |
8.0 |
mg |
| |
悬壁梁缺口冲击强度 |
-40℃ |
ASTM D256 |
40 |
J/m |
| |
|
23℃ |
ASTM D256 |
300 |
J/m |
| 热性能 |
热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
230 |
℃ |
| |
|
1.8MPa,未退火 |
ASTM D648 |
80.0 |
℃ |
| |
流动线形膨胀系数 |
|
ASTM D696 |
0.000080 |
℃ |
| |
UL阻燃等级 |
0.750mm |
UL 94 |
HB |
|
| 电气性能 |
体积电阻率 |
|
ASTM D257 |
1.0E+13 |
ohm.cm |
| |
介电强度 |
2.00mm |
ASTM D149 |
13 |
kV/mm |
| |
介电常数 |
1 kHz |
ASTM D150 |
6.50 |
|
| |
耐电弧性 |
|
ASTM D495 |
45.0 |
sec |
| |
漏电起痕指数 |
|
IEC 60112 |
600 |
V |
-
-