| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.04 |
g/cm³ |
| 物理性能 |
密度 |
|
ISO11832 |
1050 |
kg/m³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/3.8kg) |
|
ASTMD1238 |
6.0 |
g/10min |
| 物理性能 |
Meltvolume-flowrate(220°C/10.0kg) |
|
ISO11332 |
22.0 |
cm³/10min |
| 物理性能 |
收缩率-流动 |
|
ASTMD955 |
0.40to0.70 |
% |
| 机械性能 |
TensileModulus3(3.20mm,InjectionMolded) |
|
ASTMD638 |
1790 |
MPa |
| 机械性能 |
Tensilemodulus |
|
ISO527-22 |
1800 |
MPa |
| 机械性能 |
TensileStrength(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
41.4 |
MPa |
| 机械性能 |
拉伸应力(屈服) |
|
ISO527-22 |
37.0 |
MPa |
| 机械性能 |
TensileElongation(Yield,3.20mm,InjectionMolded) |
|
ASTMD638 |
3.0 |
% |
| 机械性能 |
拉伸应变(屈服) |
|
ISO527-22 |
2.3 |
% |
| 机械性能 |
Nominalstrainatbreak |
|
ISO527-22 |
>50 |
% |
| 机械性能 |
FlexuralModulus4(3.20mm,InjectionMolded) |
|
ASTMD790 |
2000 |
MPa |
| 机械性能 |
FlexuralStrength4(3.20mm,InjectionMolded) |
|
ASTMD790 |
58.6 |
MPa |
| 冲击性能 |
Charpynotchedimpactstrength(23°C) |
|
ISO179/1eA2 |
16.0 |
kJ/m² |
| 冲击性能 |
简支梁缺口冲击强度(-30°C) |
|
ISO179/1eA2 |
8.00 |
kJ/m² |
| 冲击性能 |
简支梁冲击强度(23°C) |
|
ISO179/1eU2 |
NoBreak |
|
| 冲击性能 |
Charpyimpactstrength(-30°C) |
|
ISO179/1eU2 |
NoBreak |
|
| 冲击性能 |
悬壁梁缺口冲击强度 |
-18°C,3.20mm,InjectionMolded |
ASTMD256 |
80 |
J/m |
| 冲击性能 |
悬壁梁缺口冲击强度 |
23°C,3.20mm,注塑 |
ASTMD256 |
160 |
J/m |
| 冲击性能 |
装有测量仪表的落镖冲击 |
23°C,3.20mm,InjectionMolded,PeakEnergy |
ASTMD3763 |
32.8 |
J |
| 冲击性能 |
装有测量仪表的落镖冲击 |
23°C,3.20mm,InjectionMolded,TotalEnergy |
ASTMD3763 |
42.9 |
J |
| 热性能 |
载荷下热变形温度(0.45MPa,未退火) |
|
ASTMD648 |
90.6 |
°C |
| 热性能 |
DeflectionTemperatureUnderLoad(0.45MPa) |
|
ISO75-22 |
89.0 |
°C |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火) |
|
ASTMD648 |
76.7 |
°C |
| 热性能 |
DeflectionTemperatureUnderLoad(1.8MPa) |
|
ISO75-22 |
80.0 |
°C |
| 热性能 |
维卡软化温度 |
|
ASTMD15255 |
104 |
°C |
| 热性能 |
维卡软化温度(50°C/h,B(50N)) |
|
ISO3062 |
94.0 |
°C |
| 热性能 |
线形热膨胀系数-流动 |
|
ISO11359-22 |
7.8E-5 |
cm/cm/°C |