| 规格级别 | 高流动,耐热 其它 注塑 | 外观颜色 | |
| 该料用途 | 汽车外部零件、型号 | ||
| 备注说明 | 流动性高、耐热性高 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.05 | g/cm3 | |
| 熔流率 | 220℃//10.0kg | ASTM D1238 | 12 | g/10min | |
| 收缩率 | 流动,3.20mm | ASTM D955 | 0.40 到 0.70 | % | |
| 机械性能 | 洛氏硬度 | ASTM D785 | 110 | R 计秤 | |
| 抗张强度 | 屈服, 3.20mm | ASTM D638 | 49.0 | MPa | |
| 伸长率 | 屈服, 3.20mm | ASTM D638 | >5.0 | % | |
| 断裂, 3.20mm | 20 | ||||
| 弯曲模量 | 3.20mm | ASTM D790 | 2550 | MPa | |
| 弯曲强度 | 3.20mm | ASTM D790 | 78.5 | MPa | |
| 悬壁梁缺口冲击强度 | -30℃, 3.20 mm | ASTM D256 | 88 | J/m | |
| -30℃, 6.40 mm | 78 | ||||
| 23℃, 3.20 mm | 230 | ||||
| 23℃, 6.40 mm | 200 | ||||
| 热性能 | 热变形温度 | 0.45 MPa, 未退火, 6.40mm | ASTM D648 | 101 | ℃ |
| 1.8 MPa, 未退火, 6.40mm | 92.0 | ||||
|
维卡软化温度
|
|
ASTM D1525 | 99.0 | ℃ | |
|
RTI Elec
|
UL 746 | 60.0 | ℃ | ||
|
RTI Imp
|
|||||
|
RTI Str
|
|||||
|
UL 阻燃等级
|
UL 94 |
HB
|
|||
| 电气性能 | 体积电阻率 | 23℃ | ASTM D257 | 15 |
ohm·cm
|
| 介电强度 | 23℃, 1.00 mm | ASTM D149 | 33 |
kV/mm
|
|
|
耐电弧性
|
ASTM D495 | 6.0 |
sec
|
||
| 相比耐漏电起痕指数 | UL 746 |
PLC 0
|
|||