| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
23℃，24小时 |
ASTM D-570 |
|
% |
| 物理性能 |
泰伯磨耗量 |
(1000g,CS-17)23℃ |
ASTM D-1044 |
|
mg/1000次 |
| 比重 |
|
ASTM D-792 |
|
|
| 机械性能 |
抗拉屈服强度 |
23℃ |
ASTM D-638 |
|
Kg/cm2 |
| 挠曲模量 |
23℃ |
ASTM D-790 |
|
Kg/cm2 |
| 抗剪强度 |
23℃ |
ASTM D-732 |
|
Kg/cm2 |
| 挠曲模量 |
80℃ |
ASTM D-790 |
|
Kg/cm2 |
| 断裂伸长率 |
80℃ |
ASTM D-638 |
|
% |
| 断裂伸长率 |
23℃ |
ASTM D-638 |
|
% |
| IZOD冲击强度 |
-40℃，无缺口1/8 |
|
|
kg·cm/cm2 |
| IZOD冲击强度 |
-40℃，无缺口1/2 |
ASTM D-256 |
|
kg·cm/cm |
| 压缩强度 |
23℃ |
ASTM D-695 |
|
Kg/cm2 |
| 洛氏硬度 |
23℃ |
ASTM D-785 |
|
M-标度 |
| 挠曲强度 |
23℃ |
ASTM D-790 |
|
Kg/cm2 |
| 挠曲强度 |
80℃ |
ASTM D-790 |
|
Kg/cm2 |
| IZOD冲击强度 |
23℃，V-缺口1/2 |
ASTM D-256 |
|
kg·cm/cm |
| 挠曲模量 |
-40℃ |
ASTM D-790 |
|
Kg/cm2 |
| 断裂伸长率 |
-40℃ |
ASTM D-638 |
|
% |
| 压缩强度 |
-40℃ |
ASTM D-695 |
| 无水｜1.9%水 |
无水｜1.9%水 |
| 2600｜- |
2600｜- |
|
Kg/cm2 |
| 洛氏硬度 |
23℃ |
ASTM D-785 |
|
R-标度 |
| 抗拉屈服强度 |
-40℃ |
ASTM D-638 |
|
Kg/cm2 |
| 压缩强度 |
80℃ |
ASTM D-695 |
| 无水｜1.9%水 |
无水｜1.9%水 |
| 1000｜- |
1000｜- |
|
Kg/cm2 |
| IZOD冲击强度 |
23℃，无缺口1/8 |
|
|
kg·cm/cm2 |
| 抗拉屈服强度 |
80℃ |
ASTM D-638 |
|
Kg/cm2 |
| 挠曲强度 |
-40℃ |
ASTM D-790 |
|
Kg/cm2 |
| 电气性能 |
损耗因数 |
106Hz |
ASTM D-150 |
|
|
| 介电常数 |
106Hz |
ASTM D-150 |
|
|
| 抗电弧性 |
1/8" |
ASTM D-495 |
|
s |
| 介电强度 |
1/8" |
ASTM D-149 |
|
KV/mm |
| 介电常数 |
103Hz |
ASTM D-150 |
|
|
| 损耗因数 |
103Hz |
ASTM D-150 |
|
|
| 损耗因数 |
50Hz |
ASTM D-150 |
| 无水｜1.9%水 |
无水｜1.9%水 |
| 0.03｜0.16 |
0.03｜- |
|
|
| 体积电阻率 |
|
ASTM D-257 |
|
Ω.cm |
| 热性能 |
熔点 |
|
差示扫描测热计DSC |
|
℃ |
| 热挠曲温度 |
4.6kg/cm2 |
ASTM D-648 |
|
℃ |
| UL-94抗燃级 |
1/16" |
UL 94 |
|
|
| 线性热膨胀系数 |
|
ASTM D-696 |
|
×10-5cm/cm/℃ |
| 热挠曲温度 |
18.6kg/cm2 |
ASTM D-648 |
|
℃ |
| 比热 |
|
|
|
Cal/g·℃ |
| 其它性能 |
强化含量 |
|
|
|
WT% |