| 规格级别 | 耐热 汽车部件 注塑 | 外观颜色 | |
| 该料用途 | 车内部零件、汽车外部零件、型号 | ||
| 备注说明 | 耐热性高 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.05 | g/cm3 | |
| 熔流率 | 220℃//10.0kg | ASTM D1238 | 15 | g/10min | |
| 收缩率 | 流动,3.20mm | ASTM D955 | 0.40 到 0.70 | % | |
| 机械性能 | 洛氏硬度 | ASTM D785 | 110 | R 计秤 | |
| 抗张强度 | 屈服, 3.20mm | ASTM D638 | 47.1 | MPa | |
| 伸长率 | 屈服, 3.20mm | ASTM D638 | >5.0 | % | |
| 断裂, 3.20mm | 25 | ||||
| 弯曲模量 | 6.40mm | ASTM D790 | 2600 | MPa | |
| 弯曲强度 | 6.40mm | ASTM D790 | 78.5 | MPa | |
| 悬壁梁缺口冲击强度 | -30℃, 3.20 mm | ASTM D256 | 120 | J/m | |
| -30℃, 6.40 mm | 98 | ||||
| 23℃, 3.20 mm | 290 | ||||
| 23℃, 6.40 mm | 270 | ||||
| 热性能 | 热变形温度 | 0.45 MPa, 未退火, 6.40mm | ASTM D648 | 99.0 | ℃ |
| 1.8 MPa, 未退火, 6.40mm | 91.0 | ||||
| 维卡软化温度 | ASTM D1525 | 99.0 | ℃ | ||
| RTI Elec | UL 746 | 60.0 | ℃ | ||
| RTI Imp | |||||
| RTI Str | |||||
| UL 阻燃等级 | UL 94 | HB | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 14 |
ohm·cm
|
|
| 介电强度 | 1.00mm | ASTM D149 | 30 |
kV/mm
|
|
|
耐电弧性
|
ASTM D495 |
6.00
|
sec
|
||
| 相比耐漏电起痕指数 | IEC 60112 |
PLC 0
|
|||