| 规格级别 | 矿物增强,高刚性 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 玻璃/矿物60%。 性能特点：芳香，高刚性，耐气候影响性能良好。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.74 | g/cm3 | |
| 熔流率 | ASTM D1238 | 9.0 | g/10min | ||
| 流动收缩率 | 1.00mm | ASTM D955 | 0.10-0.20 | % | |
| 3.00mm | ASTM D955 | 0.20-0.50 | % | ||
| 吸水率 | 24 hr | ASTM D570 | 0.60 | % | |
| 平衡，65%RH | ASTM D570 | 1.4 | % | ||
| 洛氏硬度 | R 计秤 | ASTM D785 | 120 | ||
| 机械性能 | 屈服抗张强度 | -40℃ | ASTM D638 | 195 | MPa |
| 23℃ | ASTM D638 | 134 | MPa | ||
| 80℃ | ASTM D638 | 77.0 | MPa | ||
| 断裂伸长率 | 23℃ | ASTM D638 | 1.3 | % | |
| 弯曲模量 | -40℃ | ASTM D790 | 18500 | MPa | |
| 23℃ | ASTM D790 | 17800 | MPa | ||
| 80℃ | ASTM D790 | 7300 | MPa | ||
| 屈服弯曲强度 | -40℃ | ASTM D790 | 280 | MPa | |
| 23℃ | ASTM D790 | 210 | MPa | ||
| 80℃ | ASTM D790 | 112 | MPa | ||
| 悬壁梁缺口冲击强度 | -40℃ | ASTM D256 | 70 | J/m | |
| 23℃ | ASTM D256 | 85 | J/m | ||
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 220 | ℃ |
| 1.8MPa,未退火 | ASTM D648 | 200 | ℃ | ||
| UL阻燃等级 | UL 94 | HB | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 1.0E+13 | ohm.cm | |
| 介电强度 | 2.00mm | ASTM D149 | 21 | kV/mm | |