PA6 | TY-791GT
生产厂家：日本东洋
规格用途
| 规格级别 |
玻纤增强 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
玻纤增强55%。 性能特点：芳香，外观良好。 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.64 |
g/cm3 |
| |
熔流率 |
|
ASTM D1238 |
10 |
g/10min |
| |
流动收缩率 |
1.00mm |
ASTM D955 |
0.10-0.20 |
% |
| |
|
3.00mm |
ASTM D955 |
0.20-0.50 |
% |
| |
吸水率 |
24 hr |
ASTM D570 |
0.80 |
% |
| |
|
平衡，65%RH |
ASTM D570 |
1.0 |
% |
| |
洛氏硬度 |
R 计秤 |
ASTM D785 |
120 |
|
| 机械性能 |
屈服抗张强度 |
-40℃ |
ASTM D638 |
250 |
MPa |
| |
|
23℃ |
ASTM D638 |
165 |
MPa |
| |
|
80℃ |
ASTM D638 |
105 |
MPa |
| |
断裂伸长率 |
23℃ |
ASTM D638 |
2.0 |
% |
| |
弯曲模量 |
-40℃ |
ASTM D790 |
15000 |
MPa |
| |
|
23℃ |
ASTM D790 |
13000 |
MPa |
| |
|
80℃ |
ASTM D790 |
5000 |
MPa |
| |
屈服弯曲强度 |
-40℃ |
ASTM D790 |
320 |
MPa |
| |
|
23℃ |
ASTM D790 |
280 |
MPa |
| |
|
80℃ |
ASTM D790 |
160 |
MPa |
| |
压缩强度 |
23℃ |
ASTM D695 |
150 |
MPa |
| |
悬壁梁缺口冲击强度 |
-40℃ |
ASTM D256 |
85 |
J/m |
| |
|
23℃ |
ASTM D256 |
180 |
J/m |
| 热性能 |
热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
217 |
℃ |
| |
|
1.8MPa,未退火 |
ASTM D648 |
217 |
℃ |
| |
流动线形膨胀系数 |
|
ASTM D696 |
0.000019 |
cm/cm/℃ |
| |
UL阻燃等级 |
|
UL 94 |
HB |
|
| 电气性能 |
体积电阻率 |
|
ASTM D257 |
1.0E+15 |
ohm.cm |
| |
介电强度 |
2.00mm |
ASTM D149 |
21 |
kV/mm |
| |
耐电弧性 |
|
ASTM D495 |
94.0 |
sec |
| |
漏电起痕指数 |
|
IEC 60112 |
550 |
V |
-
-