PA6 | T-808-02
生产厂家：日本东洋
规格用途
| 规格级别 |
阻燃 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.18 |
g/cm3 |
| |
熔流率 |
|
ASTM D1238 |
40 |
g/10min |
| |
流动收缩率 |
1.00mm |
ASTM D955 |
0.40-0.80 |
% |
| |
|
3.00mm |
ASTM D955 |
1.0-1.3 |
% |
| |
吸水率 |
24 hr |
ASTM D570 |
1.3 |
% |
| |
|
平衡，65%RH |
ASTM D570 |
3.0 |
% |
| |
洛氏硬度 |
R 计秤 |
ASTM D785 |
120 |
|
| 机械性能 |
屈服抗张强度 |
-40℃ |
ASTM D638 |
90.0 |
MPa |
| |
|
23℃ |
ASTM D638 |
40.0 |
MPa |
| |
|
80℃ |
ASTM D638 |
20.0 |
MPa |
| |
断裂伸长率 |
23℃ |
ASTM D638 |
15 |
% |
| |
弯曲模量 |
-40℃ |
ASTM D790 |
5100 |
MPa |
| |
|
23℃ |
ASTM D790 |
1300 |
MPa |
| |
|
80℃ |
ASTM D790 |
500 |
MPa |
| |
屈服弯曲强度 |
-40℃ |
ASTM D790 |
120 |
MPa |
| |
|
23℃ |
ASTM D790 |
45.0 |
MPa |
| |
|
80℃ |
ASTM D790 |
26.0 |
MPa |
| |
压缩强度 |
23℃ |
ASTM D695 |
80.0 |
MPa |
| |
悬壁梁缺口冲击强度 |
-40℃ |
ASTM D256 |
45 |
J/m |
| |
|
23℃ |
ASTM D256 |
180 |
J/m |
| 热性能 |
热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
190 |
℃ |
| |
|
1.8MPa,未退火 |
ASTM D648 |
84.0 |
℃ |
| |
流动线形膨胀系数 |
|
ASTM D696 |
0.000070 |
cm/cm/℃ |
| |
UL阻燃等级 |
0.750mm |
UL 94 |
V-0 |
|
| 电气性能 |
体积电阻率 |
|
ASTM D257 |
1.0E+12 |
ohm.cm |
| |
介电强度 |
2.00mm |
ASTM D149 |
17 |
kV/mm |
| |
介电常数 |
1 kHz |
ASTM D150 |
5.20 |
|
| |
耗散因数 |
1 kHz |
ASTM D150 |
0.080 |
|
| |
耐电弧性 |
|
ASTM D495 |
105 |
sec |
| |
漏电起痕指数 |
|
IEC 60112 |
600 |
V |
-
-
TOP