PA6 | T-422VOR
生产厂家：日本东洋
规格用途
| 规格级别 |
矿物增强 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
矿物填料23%。 性能特点：卤化。 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792 |
1.56 |
g/cm3 |
| |
熔流率 |
|
ASTM D1238 |
20 |
g/10min |
| |
流动收缩率 |
1.00mm |
ASTM D955 |
0.10-0.20 |
% |
| |
|
3.00mm |
ASTM D955 |
0.30-0.60 |
% |
| |
吸水率 |
24 hr |
ASTM D570 |
0.50 |
% |
| |
|
平衡，65%RH |
ASTM D570 |
1.8 |
% |
| |
洛氏硬度 |
R 计秤 |
ASTM D785 |
118 |
|
| 机械性能 |
屈服抗张强度 |
-40℃ |
ASTM D638 |
61.0 |
MPa |
| |
|
23℃ |
ASTM D638 |
38.0 |
MPa |
| |
|
80℃ |
ASTM D638 |
24.0 |
MPa |
| |
断裂伸长率 |
23℃ |
ASTM D638 |
4.5 |
% |
| |
弯曲模量 |
-40℃ |
ASTM D790 |
6400 |
MPa |
| |
|
23℃ |
ASTM D790 |
4400 |
MPa |
| |
|
80℃ |
ASTM D790 |
1200 |
MPa |
| |
屈服弯曲强度 |
-40℃ |
ASTM D790 |
104 |
MPa |
| |
|
23℃ |
ASTM D790 |
63.0 |
MPa |
| |
|
80℃ |
ASTM D790 |
38.0 |
MPa |
| |
压缩强度 |
23℃ |
ASTM D695 |
45.0 |
MPa |
| |
抗泰伯磨耗 |
1000Cycles,CS-17转轮 |
ASTM D1044 |
32.0 |
mg |
| |
悬壁梁缺口冲击强度 |
-40℃ |
ASTM D256 |
45 |
J/m |
| |
|
23℃ |
ASTM D256 |
70 |
J/m |
| 热性能 |
热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
205 |
℃ |
| |
|
1.8MPa,未退火 |
ASTM D648 |
160 |
℃ |
| |
流动线形膨胀系数 |
|
ASTM D696 |
0.000042 |
℃ |
| |
UL阻燃等级 |
0.730mm |
UL 94 |
V-0 |
|
| 电气性能 |
体积电阻率 |
|
ASTM D257 |
1.0E+12 |
ohm.cm |
| |
介电强度 |
2.00mm |
ASTM D149 |
20 |
kV/mm |
| |
耐电弧性 |
|
ASTM D495 |
15.0 |
sec |
| |
漏电起痕指数 |
|
IEC 60112 |
350 |
V |
-
-