| 规格级别 | 增强 其它 注塑 | 外观颜色 | 本色 |
| 该料用途 | |||
| 备注说明 | 增强20% | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 长度模收缩率 | ASTM D-955 | 1.57 | % | |
| 面积模收缩率 | ASTM D-955 | 2.96 | % | ||
| 比重 | ASTM D-792 | 1.06 | g/cm3 | ||
| 机械性能 | 洛氏硬度 | ASTM D-2240 | 69.3 | ||
| 伸长率 | 1/8"smaple | ASTM D-638 | 35 | kg/cm3 | |
| 抗张降伏点 | 1/8"smaple | ASTM D-638 | 442 | kg/cm3 | |
| 抗张系数 | 1/8"smaple | ASTM D-638 | 6802 | kg/cm3 | |
| 抗折系数 | 1/8"smaple | ASTM D-790 | 15740 | kg/cm3 | |
| 抗张断裂点 | 1/8"smaple | ASTM D-638 | 356 | kg/cm3 | |
| 缺口冲击值 | 1/8×1/2×5/2sample,23℃ | ASTM D-256 | 83.80 | kg.cm/cm | |
| 缺口冲击值 | 1/4×1/2×5/2sample,23℃ | ASTM D-256 | 83.56 | kg.cm/cm | |
| 抗张强度 | 1/8"smaple | ASTM D-790 | 620 | kg/cm3 | |
| 热性能 | 热变形温度 | 1/8"×1/2"×5"sample,18.6kg/cm2 | ASTM D-648 | 48 | ℃ |