ABS | HI-100H
生产厂家：LG化学
规格用途
| 规格级别 |
其它 专用粒料 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
|
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
200℃/5kg |
ASTM D-1238 |
1 |
g/10min |
| 熔体流动速率 |
220℃/10kg |
ASTM D-1238 |
11 |
g/10min |
| 熔体流动速率 |
230℃/3.8kg |
ASTM D-1238 |
3 |
g/10min |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.02 |
g/cc |
| 成型收缩率 |
|
ASTM D-955 |
0.4-0.7 |
% |
| 机械性能 |
拉伸强度 |
50mm/min |
ASTM D-638 |
380 |
kg/cm2 |
| 拉伸模量 |
1mm/min |
ASTM D-638 |
17200 |
kg/cm2 |
| 屈服伸长率 |
50mm/min |
ASTM D-638 |
6 |
% |
| 断裂伸长率 |
50mm/min |
ASTM D-638 |
25 |
% |
| 弯曲强度 |
15mm/min |
ASTM D-790 |
595 |
kg/cm2 |
| 弯曲模量 |
15mm/min |
ASTM D-790 |
19300 |
kg/cm2 |
| IZOD缺口冲击强度 |
1/4" 23℃ |
ASTM D-256 |
52 |
kg.cm/cm |
| IZOD缺口冲击强度 |
1/4" -30℃ |
ASTM D-256 |
31 |
kg.cm/cm |
| IZOD缺口冲击强度 |
1/8" 23℃ |
ASTM D-256 |
51 |
kg.cm/cm |
| IZOD缺口冲击强度 |
1/8" -30℃ |
ASTM D-256 |
34 |
kg.cm/cm |
| 洛氏硬度 |
|
ASTM D-785 |
94 |
R-scale |
| 热性能 |
热变形温度 |
18.5kg/cm2 1/4"退火 |
ASTM D-648 |
92 |
℃ |
| 热变形温度 |
18.5kg/cm2 1/4"未退火 |
ASTM D-648 |
85 |
℃ |
| 热变形温度 |
4.6kg/cm21/4"退火 |
ASTM D-648 |
92 |
℃ |
| 热变形温度 |
4.6kg/cm21/4" 未退火 |
ASTM D-648 |
89 |
℃ |
| 维卡软化点 |
5kg, 50℃/h |
ASTM D-1525 |
93 |
℃ |
| 阻燃等级 |
1/8" |
UL94 |
HB |
calss |
| 阻燃等级 |
1/16" |
UL94 |
HB |
calss |
-
-