| 规格级别 | 其它 其它 挤出,注塑 | 外观颜色 | |
| 该料用途 | 用于旅行箱,工具箱,机车零件,低温用产品,安全帽,公交箱,鞋跟,押制管件等 | ||
| 备注说明 | 超高耐冲击型,广泛用于押出成型/射出成型,超高耐冲击强度,加工性佳,热成型佳。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 融体流动速率 | 200℃/5kg | ASTM D-1238 | 1.0 | g/10min |
| 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 10 | g/10min | |
| 密度 | ASTM D-792 | 1.03 | |||
| 吸水率 | ASTM D-570 | 0.3 | WT% | ||
| 物理性能 | 成型收缩率 | ASTM D-955 | 0.4 | % | |
| 机械性能 | IZOD缺口冲击强度 | 23℃1/2" | ASTM D-256 | 31 (5.5) | kg.cm/cm(Ft.1b/in) |
| IZOD缺口冲击强度 | 1/8" 23℃ | ASTM D-256 | 45 (7.0) | kg.cm/cm(Ft.1b/in) | |
| 降伏点抗张强度 | 23℃ | ASTM D-638 | 410 | kg/cm2 | |
| 降伏点抗张强度 | 23℃ | ASTM D-256 | 5800 | psi | |
| 断裂点抗张强度 | 1/8" | ASTM D-638 | 360 | kg/cm2 | |
| 断裂点抗张强度 | 1/8" | ASTM D-638 | 5100 | psi | |
| 断裂伸长率 | 1/8" | ASTM D-638 | 40 | % | |
| 抗折强度 | 23℃ 2.8mm/min | ASTM D-790 | 600 | kg/cm2 | |
| 抗折强度 | 23℃ 2.8mm/min | ASTM D-790 | 8500 | psi | |
| 抗折系数 | 23℃ 2.8mm/min | ASTM D-790 | 21000 | kg/cm2 | |
| 抗折系数 | 23℃ 2.8mm/min | ASTM D-790 | 300000 | psi | |
| 洛氏硬度 | 102 | ||||
| 热性能 | 热变形温度 | 未退火 | ASTM D-648 | 86 (187) | ℃(F) |
| 维卡软化点 | ASTM D-1525 | 101 | ℃ | ||
| 阻燃等级 | UL94 | HB | |||