| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
1.13 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(235°C/1.0kg) |
|
ASTMD1238 |
4.5 |
g/10min |
| 物理性能 |
吸水率 |
24hr |
ASTMD570 |
1.6 |
% |
| 物理性能 |
吸水率 |
饱和 |
ASTMD570 |
9.5 |
% |
| 物理性能 |
吸水率 |
平衡 |
ASTMD570 |
2.7 |
% |
| 物理性能 |
MoistureContent |
|
ASTMD6869 |
>800 |
ppm |
| 物理性能 |
[email protected]%SulfuricAcid |
|
|
3.01 |
|
| 物理性能 |
粘度-FAV |
|
ASTMD789 |
73.0 |
|
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
弹性模量-MD2 |
|
ASTMD882 |
710 |
MPa |
| 薄膜 |
弹性模量-TD2 |
|
ASTMD882 |
620 |
MPa |
| 薄膜 |
抗张强度2 |
MD:屈服 |
ASTMD882 |
40.0 |
MPa |
| 薄膜 |
抗张强度2 |
TD:屈服 |
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
抗张强度2 |
MD:断裂 |
ASTMD882 |
90.0 |
MPa |
| 薄膜 |
抗张强度2 |
TD:断裂 |
ASTMD882 |
90.0 |
MPa |
| 薄膜 |
伸长率2 |
MD:断裂 |
ASTMD882 |
340 |
% |
| 薄膜 |
伸长率2 |
TD:断裂 |
ASTMD882 |
360 |
% |
| 薄膜 |
二氧化碳传输速率(23°C) |
|
ASTMD1434 |
72.8 |
cm³/m²/24hr |
| 薄膜 |
氮传输速率(23°C) |
|
ASTMD1434 |
14.0 |
cm³/m²/24hr |
| 薄膜 |
氧气传输速率(23°C) |
|
ASTMD3985 |
40 |
cm³/m²/24hr |
| 薄膜 |
水气透过率(38°C,100%RH) |
|
ASTMF1249 |
990 |
g·mm/m²/atm/24hr |
| 薄膜 |
ElmendorfTearStrength |
MD:23°C |
ASTMD1922 |
590 |
N |
| 薄膜 |
ElmendorfTearStrength |
TD:23°C |
ASTMD1922 |
530 |
N |
| 薄膜 |
GravesTear |
MD:23°C |
ASTMD1004 |
3530 |
N |
| 薄膜 |
GravesTear |
TD:23°C |
ASTMD1004 |
3290 |
N |
| 薄膜 |
薄膜厚度-经测试 |
|
|
51 |
µm |
| 薄膜 |
弹性模量-MD2 |
|
ASTMD882 |
710 |
MPa |
| 薄膜 |
弹性模量-TD2 |
|
ASTMD882 |
620 |
MPa |
| 薄膜 |
抗张强度2 |
MD:屈服 |
ASTMD882 |
40.0 |
MPa |
| 薄膜 |
抗张强度2 |
TD:屈服 |
ASTMD882 |
30.0 |
MPa |
| 薄膜 |
抗张强度2 |
MD:断裂 |
ASTMD882 |
90.0 |
MPa |
| 薄膜 |
抗张强度2 |
TD:断裂 |
ASTMD882 |
90.0 |
MPa |
| 薄膜 |
伸长率2 |
MD:断裂 |
ASTMD882 |
340 |
% |
| 薄膜 |
伸长率2 |
TD:断裂 |
ASTMD882 |
360 |
% |
| 薄膜 |
二氧化碳传输速率(23°C) |
|
ASTMD1434 |
72.8 |
cm³/m²/24hr |
| 薄膜 |
氮传输速率(23°C) |
|
ASTMD1434 |
14.0 |
cm³/m²/24hr |
| 薄膜 |
氧气传输速率(23°C) |
|
ASTMD3985 |
40 |
cm³/m²/24hr |
| 薄膜 |
水气透过率(38°C,100%RH) |
|
ASTMF1249 |
990 |
g·mm/m²/atm/24hr |
| 薄膜 |
ElmendorfTearStrength |
MD:23°C |
ASTMD1922 |
590 |
N |
| 薄膜 |
ElmendorfTearStrength |
TD:23°C |
ASTMD1922 |
530 |
N |
| 薄膜 |
GravesTear |
MD:23°C |
ASTMD1004 |
3530 |
N |
| 薄膜 |
GravesTear |
TD:23°C |
ASTMD1004 |
3290 |
N |
| 热性能 |
熔融温度 |
|
|
220 |
°C |
| 补充信息 |
PunctureIndex3(23°C) |
|
|
193.4 |
kN/m |
| 补充信息 |
PunctureResistance3(23°C) |
|
|
1000 |
g |