PA6 | 1013NU2
生产厂家：泰国宇部
规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
|
| 该料用途 |
|
| 备注说明 |
特性：标准粘度、耐热、高周期 |
技术参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
成型收缩率 |
|
UBEmethod |
1.3 |
% |
| 成型收缩率 |
|
UBEmethod |
1.2 |
% |
| 吸水率 |
|
ASTM D-570 |
10.7 |
% |
| 吸水率 |
|
ASTM D-570 |
1.8 |
% |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.14 |
|
| 机械性能 |
屈服下的伸张强度 |
23° |
ASTM D-638 |
420 |
kgf/cm2 |
| 弯曲弹性率 |
23° |
ASTM D-790 |
8000 |
kgf/cm2 |
| 屈服下的伸张强度 |
-30° |
ASTM D-638 |
1100 |
kgf/cm2 |
| 挤剪强度 |
23° |
ASTM D-732 |
650 |
kgf/cm2 |
| 屈服下的伸张强度 |
-30° |
ASTM D-638 |
9000 |
kgf/cm2 |
| 弯曲强度 |
80° |
ASTM D-790 |
260 |
kgf/cm2 |
| 抗冲击强度 |
23° |
ASTM D-256 |
50 |
kgf.cm/cm |
| 断裂下的伸张强度 |
23° |
ASTM D-638 |
650 |
kgf/cm2 |
| 抗冲击强度 |
-30° |
ASTM D-256 |
4.5 |
kgf.cm/cm |
| 断裂下的延伸率 |
23° |
ASTM D-638 |
>200 |
% |
| 弯曲弹性率 |
80° |
ASTM D-790 |
7500 |
kgf/cm2 |
| 屈服下的延伸率 |
23° |
ASTM D-638 |
8 |
% |
| 屈服下的伸张强度 |
23° |
ASTM D-638 |
800 |
kgf/cm2 |
| 断裂下的延伸率 |
23° |
ASTM D-638 |
90 |
% |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
85 |
|
| TABER磨耗率 |
|
ASTM D-1044 |
7 |
mg |
| 弯曲强度 |
-30° |
ASTM D-790 |
1400 |
kgf/cm2 |
| 弯曲强度 |
23° |
ASTM D-790 |
1100 |
kgf/cm2 |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
120 |
|
| 1%变形下的压缩强度 |
23° |
ASTM D-695 |
100 |
kgf/cm2 |
| 屈服下的伸张强度 |
80° |
ASTM D-638 |
200 |
kgf/cm2 |
| 抗冲击强度 |
23° |
ASTM D-256 |
6.5 |
kgf.cm/cm |
| 弯曲弹性率 |
-30° |
ASTM D-790 |
30500 |
kgf/cm2 |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
55 |
|
| 弯曲强度 |
-30° |
ASTM D-790 |
1300 |
kgf/cm2 |
| 1%变形下的压缩强度 |
23° |
ASTM D-695 |
200 |
kgf/cm2 |
| 弯曲弹性率 |
-30° |
ASTM D-790 |
32000 |
kgf/cm2 |
| 线性热膨胀系数 |
|
ASTM D-696 |
8 |
X的10-5cm/cm/°C |
| 屈服下的伸张强度 |
80° |
ASTM D-638 |
320 |
kgf/cm2 |
| 弯曲强度 |
80° |
ASTM D-790 |
500 |
kgf/cm2 |
| 硬度（洛氏、布氏） |
23° |
ASTM D-785 |
85 |
|
| 弯曲强度 |
23° |
ASTM D-790 |
400 |
kgf/cm2 |
| 挤剪强度 |
23° |
ASTM D-732 |
600 |
kgf/cm2 |
| 弯曲弹性率 |
23° |
ASTM D-790 |
29000 |
kgf/cm2 |
| 弯曲弹性率 |
80° |
|
4000 |
|
| 电气性能 |
体积电阻率 |
|
ASTM D-257 |
1014 |
Ω.cm |
| 热性能 |
熔点 |
DSC |
|
215-225 |
°C |
| 热变形温度 |
4.6kgf/cm2 |
ASTM D-648 |
180 |
°C |
| 燃烧率 |
|
UL94 |
V-2 |
|
-
-
TOP