| 规格级别 | 外观颜色 | 黑色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.26 | g/cm³ | |
| 硬度 | 肖氏硬度(邵氏A) | ASTMD2240 | 90 | ||
| 弹性体 | 拉伸应力(50%应变) | ASTMD412 | 13.8 | MPa | |
| 弹性体 | 抗张强度(断裂) | ASTMD412 | 28.3 | MPa | |
| 弹性体 | 伸长率(断裂) | ASTMD412 | 97 | % | |
| 弹性体 | 压缩永久变形2 | 100°C,20hr | ASTMD395 | 20 | % |
| 弹性体 | 压缩永久变形2 | 100°C,70hr | ASTMD395 | 19 | % |
| 弹性体 | 压缩永久变形2 | 149°C,70hr | ASTMD395 | 230 | % |
| 老化 | 空气中拉伸强度的变化率 | 100°C,70hr | ASTMD573 | 0.0 | % |
| 老化 | 空气中拉伸强度的变化率 | 125°C,70hr | ASTMD573 | 0.0 | % |
| 老化 | 空气中拉伸强度的变化率 | 149°C,70hr | ASTMD573 | 0.20 | % |
| 老化 | 空气中极限伸长率的变化率 | 100°C,70hr | ASTMD573 | -5.0 | % |
| 老化 | 空气中极限伸长率的变化率 | 125°C,70hr | ASTMD573 | -5.0 | % |
| 老化 | 空气中极限伸长率的变化率 | 149°C,70hr | ASTMD573 | -5.0 | % |
| 老化 | 空气中硬度计硬度的变化率 | 100°C,70hr | ASTMD573 | 0.0 | |
| 老化 | 空气中硬度计硬度的变化率 | 125°C,70hr | ASTMD573 | 1.0 | |
| 老化 | 空气中硬度计硬度的变化率 | 149°C,70hr | ASTMD573 | 1.0 | |
| 老化 | 拉伸强度的变化率 | 23°C,70hr,在基准燃料A中 | ASTMD471 | -5.8 | % |
| 老化 | 拉伸强度的变化率 | 23°C,70hr,在基准燃料B中 | ASTMD471 | -42 | % |
| 老化 | 拉伸强度的变化率 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -4.0 | % |
| 老化 | 拉伸强度的变化率 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -1.3 | % |
| 老化 | 拉伸强度的变化率 | 125°C,70hr,在ASTM#1油中 | ASTMD471 | -4.0 | % |
| 老化 | 拉伸强度的变化率 | 125°C,70hr,在ASTM#3油中 | ASTMD471 | -1.0 | % |
| 老化 | 拉伸强度的变化率 | 149°C,70hr,inDieselFuel | ASTMD471 | -20 | % |
| 老化 | 拉伸强度的变化率 | 149°C,70hr,在ASTM#1油中 | ASTMD471 | -4.0 | % |
| 老化 | 拉伸强度的变化率 | 149°C,70hr,在ASTM#3油中 | ASTMD471 | -1.3 | % |
| 老化 | 极限伸长率的变化率 | 23°C,70hr,在基准燃料A中 | ASTMD471 | -2.4 | % |
| 老化 | 极限伸长率的变化率 | 23°C,70hr,在基准燃料B中 | ASTMD471 | -25 | % |
| 老化 | 极限伸长率的变化率 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -10 | % |
| 老化 | 极限伸长率的变化率 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | 3.4 | % |
| 老化 | 极限伸长率的变化率 | 125°C,70hr,在ASTM#1油中 | ASTMD471 | -10 | % |
| 老化 | 极限伸长率的变化率 | 125°C,70hr,在ASTM#3油中 | ASTMD471 | 0.0 | % |
| 老化 | 极限伸长率的变化率 | 149°C,1hr,在ASTM#1油中 | ASTMD471 | -10 | % |
| 老化 | 极限伸长率的变化率 | 149°C,70hr,inDieselFuel | ASTMD471 | -1.0 | % |
| 老化 | 极限伸长率的变化率 | 149°C,70hr,在ASTM#3油中 | ASTMD471 | 3.4 | % |
| 老化 | 硬度计硬度的变化率 | 23°C,70hr,inReferenceFuelB | ASTMD471 | -9.0 | |
| 老化 | 硬度计硬度的变化率 | 23°C,70hr,在基准燃料A中 | ASTMD471 | 0.0 | |
| 老化 | 硬度计硬度的变化率 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | 1.0 | |
| 老化 | 硬度计硬度的变化率 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -7.0 | |
| 老化 | 硬度计硬度的变化率 | 100°C,70hr,在水中 | ASTMD471 | 0.0 | |
| 老化 | 硬度计硬度的变化率 | 125°C,70hr,在ASTM#1油中 | ASTMD471 | 0.0 | |
| 老化 | 硬度计硬度的变化率 | 125°C,70hr,在ASTM#3油中 | ASTMD471 | -7.0 | |
| 老化 | 硬度计硬度的变化率 | 149°C,70hr,inDieselFuel | ASTMD471 | -12 | |
| 老化 | 硬度计硬度的变化率 | 149°C,70hr,在ASTM#1油中 | ASTMD471 | 1.0 | |
| 老化 | 硬度计硬度的变化率 | 149°C,70hr,在ASTM#3油中 | ASTMD471 | -7.0 | |
| 老化 | 体积变化 | 23°C,70hr,A级标准燃料 | ASTMD471 | 0.90 | % |
| 老化 | 体积变化 | 23°C,70hr,在基准燃料B中 | ASTMD471 | 23 | % |
| 老化 | 体积变化 | 100°C,70hr,ASTM标准油（1号） | ASTMD471 | 1.0 | % |
| 老化 | 体积变化 | 100°C,70hr,ASTM标准油（3号） | ASTMD471 | 15 | % |
| 老化 | 体积变化 | 100°C,70hr,在水中 | ASTMD471 | 2.0 | % |
| 老化 | 体积变化 | 125°C,70hr,ASTM标准油（1号） | ASTMD471 | 1.0 | % |
| 老化 | 体积变化 | 125°C,70hr,ASTM标准油（3号） | ASTMD471 | 12 | % |
| 老化 | 体积变化 | 149°C,70hr,ASTM标准油（1号） | ASTMD471 | 0.50 | % |
| 老化 | 体积变化 | 149°C,70hr,ASTM标准油（3号） | ASTMD471 | 15 | % |
| 老化 | 体积变化 | 149°C,70hr,柴油 | ASTMD471 | 20 | % |
| 热性能 | ServiceTemperature | -34到149 | °C | ||
| 补充信息 | RubberClassification3 | HNBR | |||