| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.939 |
g/cm³
|
|
|
熔流率
|
190℃
/2.16 kg
|
ASTM D1238 | 0.38 |
g/10 min
|
|
|
190℃
/2.16 kg
|
ASTM D1238 | 11 |
g/10 min
|
||
| 硬度计硬度 | 邵氏 D, 模压成型 | ASTM D2240 | 68 |
|
|
| 机械性能 |
抗张强度
|
屈服
, 模压成型
|
ASTM D638 | 19.8 |
MPa
|
|
断裂
, 模压成型
|
ASTM D638 | 33.7 |
MPa
|
||
|
伸长率
|
断裂, 模压成型
|
ASTM D638 | 1000 | % | |
| 弯曲模量 |
模压成型
|
ASTM D790B | 850 |
MPa
|
|
| 薄膜厚度 |
经测试
|
15 |
µm
|
||
|
膜耐刺穿性
|
ASTM D5748 | 5.79 |
J/cm³
|
||
|
割线模量
|
1% 正割, MD
|
ASTM D882 | 1130 |
MPa
|
|
| 2% 正割, MD | ASTM D882 | 798 |
MPa
|
||
|
1% 正割, TD
|
ASTM D882 | 1290 |
MPa
|
||
|
2% 正割, TD
|
ASTM D882 | 887 |
MPa
|
||
|
抗张强度
|
MD : 屈服
|
ASTM D882 | 16.0 |
MPa
|
|
|
TD : 屈服
|
ASTM D882 | 18.0 |
MPa
|
||
|
MD : 断裂
|
ASTM D882 | 34.8 |
MPa
|
||
|
TD : 断裂
|
ASTM D882 | 26.0 |
MPa
|
||
|
伸长率
|
MD : 断裂
|
ASTM D882 | 310 | % | |
|
TD : 断裂
|
ASTM D882 | 610 | % | ||
|
落锤冲击
|
ASTM D1709A | 100 |
g
|
||
|
埃尔曼多夫抗撕强度
|
MD
|
ASTM D1922 | 10 |
g
|
|
| TD | ASTM D1922 | 270 |
g
|
||
| 悬壁梁缺口冲击强度 | 模压成型 | ASTM D256 | 76 |
J/m
|
|
| 光学性能 | 光泽度 | ASTM D2457 | 12 | % | |
|
雾度
|
ASTM D1003 | 62 | ℃ | ||