| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.937 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/2.16kg |
ASTMD1238 |
0.30 |
g/10min |
| 物理性能 |
熔流率（熔体流动速率） |
190°C/21.6kg |
ASTMD1238 |
20 |
g/10min |
| 薄膜 |
薄膜厚度-经测试 |
|
|
13 |
µm |
| 薄膜 |
可供应的薄膜厚度 |
|
|
Minimum12µm(0.5mil) |
|
| 薄膜 |
SecantModulus-1%Secant,MD2(13µm) |
|
ASTMD882 |
790 |
MPa |
| 薄膜 |
SecantModulus-1%Secant,TD2(13µm) |
|
ASTMD882 |
965 |
MPa |
| 薄膜 |
TensileStrength-MD2(Yield,13µm) |
|
ASTMD882 |
21.0 |
MPa |
| 薄膜 |
TensileStrength-TD2(Yield,13µm) |
|
ASTMD882 |
21.0 |
MPa |
| 薄膜 |
TensileStrength-MD2(Break,13µm) |
|
ASTMD882 |
42.0 |
MPa |
| 薄膜 |
TensileStrength-TD2(Break,13µm) |
|
ASTMD882 |
41.0 |
MPa |
| 薄膜 |
TensileElongation-MD2(Break,13µm) |
|
ASTMD882 |
500 |
% |
| 薄膜 |
TensileElongation-TD2(Break,13µm) |
|
ASTMD882 |
600 |
% |
| 薄膜 |
DartDropImpact3(13µm) |
|
ASTMD1709A |
110 |
g |
| 薄膜 |
ElmendorfTearStrength-MD(13µm) |
|
ASTMD1922 |
50 |
g |
| 薄膜 |
ElmendorfTearStrength-TD(13µm) |
|
ASTMD1922 |
500 |
g |
| 热性能 |
熔融峰值温度 |
|
ASTMD3417 |
125 |
°C |