| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.938 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
0.057 |
g/10min |
| 薄膜 |
SecantModulus-MD(13µm) |
|
ASTMD882 |
641 |
MPa |
| 薄膜 |
SecantModulus-TD(13µm) |
|
ASTMD882 |
772 |
MPa |
| 薄膜 |
TensileStrength-MD(Yield,13µm) |
|
ASTMD882 |
26.3 |
MPa |
| 薄膜 |
TensileStrength-TD(Yield,13µm) |
|
ASTMD882 |
23.1 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,13µm) |
|
ASTMD882 |
88.3 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,13µm) |
|
ASTMD882 |
47.5 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,13µm) |
|
ASTMD882 |
270 |
% |
| 薄膜 |
TensileElongation-TD(Break,13µm) |
|
ASTMD882 |
390 |
% |
| 薄膜 |
TotalEnergyImpact |
13µm |
ASTMD4272 |
3.12 |
J |
| 薄膜 |
TotalEnergyImpact |
100µm |
ASTMD4272 |
5.97 |
J |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
13µm |
ASTMD1922 |
20 |
g |
| 薄膜 |
埃尔曼多夫抗撕强度-MD |
100µm |
ASTMD1922 |
420 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
13µm |
ASTMD1922 |
40 |
g |
| 薄膜 |
ElmendorfTearStrength-TD |
100µm |
ASTMD1922 |
750 |
g |